A scalable, eco-friendly ultralow-temperature approach to forming Al2O3 water-repellent cotton coatings via UV photo-annealing.

Hydrophobic coatings on cotton fabrics were successfully prepared via solution deposition of a "flat" nanoscale aluminum hydroxo cluster and a photo-assisted anneal using ultraviolet light. The coatings have a low surface roughness and high uniformity confirmed by SEM imaging and elemental analysis. The method represents a robust, scalable, and environmentally benign procedure suitable for industrial processes.

Hydrosulfide-selective ChemFETs for aqueous H2S/HS- measurement.

We have prepared and characterized hydrosulfide-selective ChemFET devices based on a nitrile butadiene rubber membrane containing tetraoctylammonium nitrate as a chemical recognition element that is applied to commercially available field-effect transistors. The sensors have fast (120 s) reversible responses, selectivity over other biologically relevant thiol-containing species, detection limits of 8 mM, and a detection range from approximately 5 to 500 mM. Sensitivities are shown to be 53 mV per decade at pH 8. Use of this compact, benchtop sensor platform requires little training - only the ability to measure DC voltage, which can be accomplished with a conventional multimeter or a simple analog data acquisition device paired with a personal computer. To the best of our knowledge, this report describes the first example of direct potentiometric measurement of the hydrosulfide ion in water.

Investigation of the physical, optical, and chemical properties of phase segregated AlCoOx thin films from a novel hexol-type cluster.

The use of a novel inorganic nanoscale cluster (Al[(µ-OH)2Co(NH3)4]3(NO3)6) was investigated for its utility as a precursor for AlCoOx films. Mixed-metal aluminum and cobalt oxide thin films were solution deposited from the novel cluster solution via the spin-coating method on Si (100) and quartz substrates. The films were annealed at increasing temperatures up to 800 °C, and characterization of these films via TEM and XRD confirms binary Co3O4 crystalline phase present in an amorphous Al2O3 network. Films are relatively smooth (Rrms < 4 nm), polycrystalline, and demonstrate a tunable optical response dominated by Co3O4 with two electronic transitions.