ABSTRACT
In this investigation, three different explosive materials have been used to improve the properties of titanium grade 2: ammonal, emulsion explosives, and plastic-bonded explosives. In order to establish the influence of explosive hardening on the properties of the treated alloys, tests were conducted, including microhardness testing, microstructure analysis, and tensile and corrosion tests. It has been found that it is possible to achieve a 40% increase in tensile strength using a plastic explosive (PBX) as an explosive material. On the other hand, the impact of the shock wave slightly decreased the corrosion resistance of titanium grade 2. The change in corrosion rate is less than 0.1µm/year, which does not significantly affect the overall corrosion resistance of the material. The reduction in corrosion resistance is probably due to the surface geometry changes as a result of explosive treatment.
ABSTRACT
A high-nitrogen compound, 2,2'-azobis(1H-imidazole-4,5-dicarbonitrile) (TCAD), was synthesized from commercially available 2-amino-1H-imidazole-4,5-dicarbonitrile. It was characterized with infrared and nuclear magnetic resonance spectroscopy. Its structure was determined by single crystal X-ray diffraction. The crystal of TCAD tetrahydrate is monoclinic, with space group P21/c with crystal parameters of a = 10.2935(2) Å, b = 7.36760(10) Å, c = 20.1447(4) Å, V = 1500.27(5) Å3, Z = 4, and F(000) = 688. Computational methods were used in order to fully optimize the molecular structure, calculate the electrostatic potential of an isolated molecule, and to compute thermodynamic parameters. TCAD has very high thermal stability with temperature of decomposition at 369 °C. Kinetics of thermal decomposition of this compound were studied and apparent energy of activation as well as the maximum safe temperature of technological process were determined.