ABSTRACT
New 3,3'-dithioalkyl-2,2'-bithiophene (SBT)-based small molecular and polymeric semiconductors are synthesized by end-capping or copolymerization with dithienothiophen-2-yl units. Single-crystal, molecular orbital computations, and optical/electrochemical data indicate that the SBT core is completely planar, likely via S(alkyl)â¯S(thiophene) intramolecular locks. Therefore, compared to semiconductors based on the conventional 3,3'-dialkyl-2,2'-bithiophene, the resulting SBT systems are planar (torsional angle <1°) and highly π-conjugated. Charge transport is investigated for solution-sheared films in field-effect transistors demonstrating that SBT can enable good semiconducting materials with hole mobilities ranging from ≈0.03 to 1.7 cm2 V-1 s-1 . Transport difference within this family is rationalized by film morphology, as accessed by grazing incidence X-ray diffraction experiments.
ABSTRACT
Al-MCM-41 mesoporous sieves were synthesized at the ambient temperature by using TEOS as silica source, Al(NO)3 x 9H2O as Al source, and cetyl trimethylammonium bromide as templating agent. The framework and surface structures of the synthesized samples were characterized by XRD, N2-adsorption/desorption isotherms, FTIR and SEM etc. The results showed that the samples were the typical Al-MCM-41 mesoporous sieves with the higher ordered-degree and specific surface area (up to 816 m2 x g(-1)) and the narrower pore diameter distribution. Controlling the highest value of Al/Si with the range of 0.06-0.13, and taking temperature programmed calcination would be beneficial to the formation of the highly ordered Al-MCM-41 mesoporous sieves. The evaluating results showed that the synthesized Al-MCM-41 molecular sieves have a higher catalytic activity for isomerization of endo-tetrahydrodicyclo-pentadiene (endo-TCD) into exo-tetrahydrodicyclo-pentadiene (exo-TCD) and adamantane.