Properties of Bis-GMA free bulk-filled resin composite based on high refractive index monomer Bis-EFMA.

With the aim to prepare Bis-GMA-free bulk-filled dental resin composite (DRC), Bis-GMA-free resin matrix was prepared by mixing Bis-EFMA with TEGDMA at two mass ratios (Bis-EFMA/TEGDMA = 50 wt/50 wt and 60 wt/40 wt), and the bulk-filled resin composites were then obtained by mixing resin matrix with silanated glass fillers at a mass ratio of 30 wt/70 wt. Bis-GMA based resin composites were used as control. Refractive indexes of resin matrixes were measured. Besides the depth of cure mentioned in ISO standard, double bond conversion (DC) and bottom/top Vickers hardness (VHN) ratio of resin composites were investigated to evaluate the curing depth. Physicochemical properties, such as flexural properties, volumetric shrinkage (VS), shrinkage stress (SS), water sorption (WS) and solubility (SL), and cytotoxicity of resin composites were tested and statistically analyzed (ANOVA, Tukey's, p = 0.05). The results showed that Bis-EFMA/TEGDMA resin matrixes had higher refractive indexes than Bis-GMA/TEGDMA resin matrixes. Viscosities of Bis-EFMA based DRCs were higher than Bis-GMA based DRCs. Bis-EFMA-based (50/50) DRC had comparable depth of cure, DC, and VHN as Bis-GMA-based (50/50) DRC (p > 0.05). Though Bis-EFMA/TEGDMA (60/40) had the highest refractive index in all resin matrix, the corresponding DRCs had the lowest depth of cure, DC, and bottom/top VHN ratio in all groups (p < 0.05). Replacing Bis-GMA with Bis-EFMA had no negative effect on flexural properties, WS and SL of DRCs, and could reduce VS and SS of DRCs. Results of CCK8 assay showed that all of DRCs had the same cytotoxicity (p > 0.05), and the thickness of sample had no influence on the cytotoxicity (p > 0.05). All the results indicated that Bis-EFMA could be used to replace Bis-GMA to prepare bulk-filled dental resin composites. According to the results of depth of cure, DC, and bottom/top VHN ratio, 50 wt/50 wt was more appropriate than 60 wt/40 wt as the mass ratio of Bis-EFMA and TEGDMA in the resin matrix for bulk-filled dental resin composites.

Preparation of Bis-GMA free dental resin composites with anti-adhesion effect against Streptococcus mutans using synthesized fluorine-containing methacrylate (DFMA).

With purpose of preparing Bis-GMA free dental resin composites (DRCs) with anti-adhesion effect against Streptococcus mutans (S. mutans), a new fluorinated dimethacrylate (DFMA) was synthesized and used as base resin of DRCs. Two reactive diluents TEGDMA and SR833s were mixed with DFMA separately to prepare resin matrixes. After mixing with inorganic fillers, two DFMA based DRCs were obtained and named as DT (DFMA/TEGDMA) and DS (DFMA/SR833s) according to the resin matrix composition. Bis-GMA based DRC (BT) was used as control. The double bond conversion (DC), bacteria adhesion, mucin adsorption, contact angle, surface free energy, volumetric shrinkage (VS), shrinkage stress (SS), water sorption (WS) and solubility (SL), flexural strength (FS) and modulus (FM) before and after water immersion were investigated, and all the results were statistically analyzed with ANOVA analysis. The results showed that DT and DS had comparable (ρ > 0.05) surface free energy which was lower than that of BT (ρ < 0.05). Compared with BT, with the same surface roughness (ρ > 0.05), less amount of S. mutans was accumulated on the surface of DT and DS (ρ < 0.05). In all DRCs, the DS had the best resistance to mucin adsorption (ρ < 0.05) due to its high hydrophobicity. Compared with BT, both DFMA based DRCs had advantages such as lower VS and SS (ρ < 0.05), lower WS and SL (ρ < 0.05), and better water resistance. The DS, which had antibacterial adhesion effect, mucin adsorption resistance, lowest VS and SL (ρ < 0.05), and the highest FS and FM no matter before or after water immersion (ρ < 0.05) was considered to have the best comprehensive properties in all DRCs.