A novel and unusual 3D luminescent coordination polymer (CP) [Zn2(3-bpah)(bpta)(H2O)]·3H2O (1), where 3-bpah denotes N,N'-bis(3-pyridinecarboxamide)-1,2-cyclohexane and H4bpta denotes 2,2',4,4'-biphenyltetracarboxylic acid, was successfully synthesized via hydrothermal methods from Zn(II) ions and 3-bpah and bpta ligands. The structure of this CP was investigated via powder X-ray diffraction (PXRD) analysis along with single crystal X-ray diffraction. Notably, 1 exhibits remarkable fluorescence behavior and stability over a wide pH range and in various pure organic solvents. More importantly, 1 can become an outstanding candidate for the selective and sensitive sensing of Fe3+, Mg2+, Cr2O72-, MnO4-, nitrobenzene (NB) and nitromethane (NM), at an extremely low detection limit. The changes in the fluorescence intensity exhibited by these six analytes in the presence of 1 over a wide pH range indicate that this polymer can be an excellent luminescent sensor. To the best of our knowledge, 1 is a rare example of a CP-based multiresponsive fluorescent sensor for metal cations, anions, and toxic organic solvents.

2.
Materials (Basel) ; 10(3)2017 Mar 19.
Article in English | MEDLINE | ID: mdl-28772673

ABSTRACT

Vanadium dioxide (VO2) thermochromic thin films with various thicknesses were grown on quartz glass substrates by radio frequency (RF)-plasma assisted oxide molecular beam epitaxy (O-MBE). The crystal structure, morphology and chemical stoichiometry were investigated systemically by X-ray diffraction (XRD), atomic force microscopy (AFM), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) analyses. An excellent reversible metal-to-insulator transition (MIT) characteristics accompanied by an abrupt change in both electrical resistivity and optical infrared (IR) transmittance was observed from the optimized sample. Remarkably, the transition temperature (TMIT) deduced from the resistivity-temperature curve was reasonably consistent with that obtained from the temperature-dependent IR transmittance. Based on Raman measurement and XPS analyses, the observations were interpreted in terms of residual stresses and chemical stoichiometry. This achievement will be of great benefit for practical application of VO2-based smart windows.