Tuning the self-assembled monolayer formation on nanoparticle surfaces with different curvatures: investigations on spherical silica particles and plane-crystal-shaped zirconia particles.

The ordering of dodecyl-chain self-assembled monolayers (SAM) on different nanoscopic surfaces was investigated by FT-IR studies. As model systems plane-crystal-shaped ZrO(2) nanoparticles and spherical SiO(2) nanoparticles were examined. The type of capping agent was chosen dependent on the substrate, therefore dodecylphosphonic acid and octadecylphosphonic acid were used for ZrO(2) and dodecyltrimethoxysilane for SiO(2) samples. The plane ZrO(2) nanocrystals yielded more ordered alkyl-chain structures whereas spherical SiO(2) nanoparticles showed significantly lower alkyl-chain ordering. Submicron-sized silica spheres revealed a significantly higher alkyl chain ordering, comparable to an analogously prepared SAM on a non-curved plane oxidized Si-wafer. In the case of ZrO(2) nanocrystals an intense alkyl-chain alignment could be disturbed by decreasing the grafting density from the maximum of 2.1 molecules/nm(2) through the variation of coupling agent concentration to lower values. Furthermore, the co-adsorption of a different coupling agent, such as phenylphosphonic acid for ZrO(2) and phenyltrimethoxysilane for SiO(2), resulted in a significantly lower alkyl-chain ordering for ZrO(2) plane crystals and for large SiO(2) spherical particles at high grafting density. An increasing amount of order-disturbing molecules leads to a gradual decrease in alkyl-chain alignment on the surface of the inorganic nanoparticles. In the case of the ZrO(2) nanoparticle system it is shown via dynamic light scattering (DLS) that the mixed monolayer formation on the particle surface impacts the dispersion quality in organic solvents such as n-hexane.

Directing alkyl chain ordering of functional phosphorus coupling agents on ZrO2.

ZrO(2) powder (6.6 m(2)/g) was modified using polymerizable phosphorus-based coupling agents (P-CAs) (i.e., phosphonic acid, phosphoric acid, and bis-phosphonic acid), resulting in densely grafted layers as determined by thermogravimetry and elemental analysis (up to 4.2 molecules/nm(2)). The applied P-CAs contained a methacrylate group, which led to the covalent incorporation of a polymerizable moiety into the grafted layer. To direct the ordering of the alkyl chains in the layer, three different approaches were evaluated with respect to their structure-directing ability by means of FT-IR and nitrogen sorption at 77 K: (i) variation of the chain length, (ii) variation of the anchoring group and (iii) comodification with a defined amount of a nonfunctional phosphonic acid (variation of the functional/nonfunctional acid ratio). It was shown that the chain length and anchoring group size have significant effects on the alkyl chain ordering and morphology of the layer.