ABSTRACT
A template-directed, sol-gel synthesis is utilized to produce crystalline RuO2 nanowires. Crystalline nanowires with a diameter of 128 ± 15 nm were synthesized after treating the nanowires at 600 °C in air. Analysis of these nanowires by X-ray powder diffraction revealed the major crystalline phase to be tetragonal RuO2 with a small quantity of metallic ruthenium present. Further analysis of the nanowire structures by high-resolution transmission electron microscopy reveals that they are polycrystalline and are composed of interconnected, highly crystalline, nanoparticles having an average size of â¼25 nm. Uniform 3 nm Pt nanoparticles were dispersed on the surface of RuO2 nanowires using an ambient, solution-based technique yielding a hybrid catalyst for methanol oxidation. Linear sweep voltammograms (LSVs) and chronoamperometry performed in the presence of methanol in an acidic electrolyte revealed a significant enhancement in the onset potential, mass activity, and long-term stability compared with analogous Pt nanoparticles supported on commercially available Vulcan XC-72R carbon nanoparticles. Formic acid oxidation LSVs and CO stripping voltammetry revealed that the RuO2-supported Pt nanoparticles exhibit significantly higher CO tolerance, which leads to higher catalytic stability over a period of several hours. X-ray photoelectron spectroscopy results suggest that crystalline RuO2 leads to less-significant oxidation of the Pt surface relative to more widely studied hydrous RuO2 supports, thereby increasing catalytic performance.