ABSTRACT
Polymer composites reinforced with natural fabric have recently been investigated as possible ballistic armor for personal protection against different levels of ammunition. In particular, fabric made of fique fibers, which is extracted from the leaves of the Furcraea andina, was applied as reinforcement for polymer composites used in a multilayered armor system (MAS). The superior performance of the fique fabric composites as a second MAS layer motivated this brief report on the determination of the absorbed energy and capability to limit velocity in the stand-alone ballistic tests. The single plates of epoxy composites, which were reinforced with up to 50 vol% of fique fabric, were ballistic tested as targets against 7.62 mm high-speed, ~840 m/s, impact ammunition for the first time. The results were statistically analyzed by the Weibull method and ANOVA. The absorbed energies of the 200-219 J and limit velocities of 202-211 m/s were found statistically similar to the epoxy composites reinforced with the fique fabric from 15 to 50 vol%. Predominantly, these findings are better than those reported for the plain epoxy and aramid fabric (KevlarTM) used as stand-alone plates with the same thickness. Macrocracks in the 15 and 30 vol% fique fabric composites compromise their application as armor plates. The delamination rupture mechanism was revealed by scanning electron microscopy. By contrast, the integrity was maintained in the 40 and 50 vol% composites, ensuring superior ballistic protection compared to the use of KevlarTM.
ABSTRACT
In recent decades, the unique characteristics of natural fibers have promoted their use as reinforcement in polymeric composites. This is verified in several industrial sectors, from packaging to automotive and civil construction. Among the natural fibers, the raffia fiber extracted from the palm tree Raphia vinifera and introduced in the Amazon region a long time ago; started to be considered for the production of polymeric composites only in recent years. For the first time, the effect of raffia fiber length and its alkali treatment on the mechanical properties of a polymer composite was disclosed. Tensile tests were performed in composites with raffia fibers randomly dispersed into terephthalate-based unsaturated polyester resin. The results showed an increase in the Young's moduli, confirmed by ANOVA, for the composite with both untreated and alkali-treated fibers in comparison to the plain polyester, which characterizes a stiffening effect. The composites with alkali treated fibers exhibited similar tensile strength values for all lengths; however, their strengths are lower than those for the untreated condition due to a weak raffia fiber/polyester matrix adhesion. Therefore, this work fills the current knowledge gap on raffia fiber incorporation in polyester matrix and valorizes this abundant Brazilian resource, providing additional information towards the use of raffia fiber in polymer composites.
ABSTRACT
The replacement of synthetic fibers by natural fibers has, in recent decades, been the subject of intense research, particularly as reinforcement of composites. In this work, the lesser known tucum fiber, extracted from the leaves of the Amazon Astrocaryum vulgare palm tree, is investigated as a possible novel reinforcement of epoxy composites. The tucum fiber was characterized by pullout test for interfacial adhesion with epoxy matrix. The fiber presented a critical length of 6.30 mm, with interfacial shear strength of 2.73 MPa. Composites prepared with different volume fractions of 20 and 40% tucum fiber were characterized by tensile and Izod impact tests, as well as by ballistic impact energy absorption using .22 ammunition. A cost analysis compared the tucum fiber epoxy composites with other natural and synthetic fiber reinforced epoxy composites. The results showed that 40 vol% tucum fiber epoxy composites increased the tensile strength by 104% and the absorbed Izod impact energy by 157% in comparison to the plain epoxy, while the ballistic performance of the 20 vol% tucum fiber composites increased 150%. These results confirmed for the first time a reinforcement effect of the tucum fiber to polymer composites. Moreover, these composites exhibit superior cost effectiveness, taking into account a comparison made with others epoxy polymer composites.
ABSTRACT
Natural-fiber-reinforced polymer composites have recently drawn attention as new materials for ballistic armor due to sustainability benefits and lower cost as compared to conventional synthetic fibers, such as aramid and ultra-high-molecular-weight polyethylene (UHMWPE). In the present work, a comparison was carried out between the ballistic performance of UHMWPE composite, commercially known as Dyneema, and epoxy composite reinforced with 30 vol % natural fibers extracted from pineapple leaves (PALF) in a hard armor system. This hard armor system aims to provide additional protection to conventional level IIIA ballistic armor vests, made with Kevlar, by introducing the PALF composite plate, effectively changing the ballistic armor into level III. This level of protection allows the ballistic armor to be safely subjected to higher impact projectiles, such as 7.62 mm caliber rifle ammunition. The results indicate that a hard armor with a ceramic front followed by the PALF/epoxy composite meets the National Institute of Justice (NIJ) international standard for level III protection and performs comparably to that of the Dyneema plate, commonly used in armor vests.
ABSTRACT
Natural lignocellulosic fibers and corresponding fabrics have been gaining notoriety in recent decades as reinforcement options for polymer matrices associated with industrially applied composites. These natural fibers and fabrics exhibit competitive properties when compared with some synthetics such as glass fiber. In particular, the use of fabrics made from natural fibers might be considered a more efficient alternative, since they provide multidirectional reinforcement and allow the introduction of a larger volume fraction of fibers in the composite. In this context, it is important to understand the mechanical performance of natural fabric composites as a basic condition to ensure efficient engineering applications. Therefore, it is also important to recognize that ramie fiber exhibiting superior strength can be woven into fabric, but is the least investigated as reinforcement in strong, tough polymers to obtain tougher polymeric composites. Accordingly, this paper presents the preparation of epoxy composite containing 30 vol.% Boehmeria nivea fabric by vacuum-assisted resin infusion molding technique and mechanical behavior characterization of the prepared composite. Obtained results are explained based on the fractography studies of tested samples.
ABSTRACT
Composites with sustainable natural fibers are currently experiencing remarkably diversified applications, including in engineering industries, owing to their lower cost and density as well as ease in processing. Among the natural fibers, the fiber extracted from the leaves of the Amazonian curaua plant (Ananas erectifolius) is a promising strong candidate to replace synthetic fibers, such as aramid (Kevlar™), in multilayered armor system (MAS) intended for ballistic protection against level III high velocity ammunition. Another remarkable material, the graphene oxide is attracting considerable attention for its properties, especially as coating to improve the interfacial adhesion in polymer composites. Thus, the present work investigates the performance of graphene oxide coated curaua fiber (GOCF) reinforced epoxy composite, as a front ceramic MAS second layer in ballistic test against level III 7.62 mm ammunition. Not only GOCF composite with 30 vol% fibers attended the standard ballistic requirement with 27.4 ± 0.3 mm of indentation comparable performance to Kevlar™ 24 ± 7 mm with same thickness, but also remained intact, which was not the case of non-coated curaua fiber similar composite. Mechanisms of ceramic fragments capture, curaua fibrils separation, curaua fiber pullout, composite delamination, curaua fiber braking, and epoxy matrix rupture were for the first time discussed as a favorable combination in a MAS second layer to effectively dissipate the projectile impact energy.