ABSTRACT
Using palladium-catalyzed Suzuki polycondensation, we synthesized new light-emitting fluorene copolymers containing the dicyano derivatives of stilbene and phenanthrene and characterized them by gel permeation chromatography, UV-vis absorption spectroscopy, spectrofluorimetry, and cyclic voltammetry. The photoluminescence spectra of the synthesized polymers show significant energy transfer from the fluorene segments to the dicyanostilbene and 9,10-dicyanophenanthrene units, which is in agreement with the data of theoretical calculations. OLEDs based on these polymers were fabricated with an ITO/PEDOT-PSS (35 nm)/p-TPD (30 nm)/PVK (5 nm)/light emitting layer (70-75 nm)/PF-PO (20 nm)/LiF (1 nm)/Al (80 nm) configuration. Examination of their electroluminescence revealed that copolymers of fluorene with dicyanostilbene show yellow-green luminescence, while polymers with 9,10-dicyanophenanthrene have a greenish-blue emission. The 9,10-dicyanophenanthrene units have a more rigid structure compared to dicyanostilbene and, in OLEDs based on them, an increase in maximum brightness is observed with an increase in the content of the additive to the polymer chain. In particular, the device using fluorene copolymer with 9,10-dicyanophenanthrene (2.5 mol%) exhibited a maximum brightness of 9230 cd/m2 and a maximum current efficiency of 3.33 cd/A.
ABSTRACT
Quantum dots (QDs) are promising candidates for producing bright, color-pure, cost-efficient, and long-lasting QD-based light-emitting diodes (QDLEDs). However, one of the significant problems in achieving high efficiency of QDLEDs is the imbalance between the rates of charge-carrier injection into the emissive QD layer and their transport through the device components. Here we investigated the effect of the parameters of the deposition of a poly (methyl methacrylate) (PMMA) electron-blocking layer (EBL), such as PMMA solution concentration, on the characteristics of EBL-enhanced QDLEDs. A series of devices was fabricated with the PMMA layer formed from acetone solutions with concentrations ranging from 0.05 to 1.2 mg/mL. The addition of the PMMA layer allowed for an increase of the maximum luminance of QDLED by a factor of four compared to the control device without EBL, that is, to 18,671 cd/m2, with the current efficiency increased by an order of magnitude and the turn-on voltage decreased by ~1 V. At the same time, we have demonstrated that each particular QDLED characteristic has a maximum at a specific PMMA layer thickness; therefore, variation of the EBL deposition conditions could serve as an additional parameter space when other QDLED optimization approaches are being developed or implied in future solid-state lighting and display devices.