ABSTRACT
A cytocompatible porous scaffold mimicking the properties of extracellular matrices (ECMs) has great potential in promoting cellular attachment and proliferation for tissue regeneration. A biomimetic scaffold was prepared using silk fibroin (SF)/sodium alginate (SA) in which regular and uniform pore morphology can be formed through a facile freeze-dried method. The scanning electron microscopy (SEM) studies showed the presence of interconnected pores, mostly spread over the entire scaffold with pore diameter around 54~532 µm and porosity 66~94%. With significantly better water stability and high swelling ratios, the blend scaffolds crosslinked by 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC) provided sufficient time for the formation of neo-tissue and ECMs during tissue regeneration. Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD) results confirmed random coil structure and silk I conformation were maintained in the blend scaffolds. What's more, FI-TR spectra demonstrated crosslinking reactions occurred actually among EDC, SF and SA macromolecules, which kept integrity of the scaffolds under physiological environment. The suitable pore structure and improved equilibrium swelling capacity of this scaffold could imitate biochemical cues of natural skin ECMs for guiding spatial organization and proliferation of cells in vitro, indicating its potential candidate material for soft tissue engineering.
Subject(s)
Alginates/chemistry , Biomimetic Materials/chemistry , Fibroins/chemistry , Tissue Engineering , Tissue Scaffolds , Animals , Bombyx , Cell Adhesion , Cell Line , Cell Survival , Ethyldimethylaminopropyl Carbodiimide/chemistry , Fluorescent Dyes/chemistry , Freeze Drying , Glucuronic Acid/chemistry , Hexuronic Acids/chemistry , Mice , Microscopy, Electron, Scanning , Porosity , Spectroscopy, Fourier Transform Infrared , Temperature , Water/chemistry , X-Ray DiffractionABSTRACT
In this study, to obtain biomedical polyurethane elastomers with good mechanical properties and biocompatibility, a series of polycarbonate urethanes were synthesized via a two-step solution of polymerization method using the poly(1,6-hexanediol)carbonate diols (PCDL) as the soft segment, 4,4'-methylenebis(cyclohexyl isocyanate) (H12MDI), 1,6-hexamethylene diisocyanate (HDI) and 1,4-butanediol (BDO) as the hard segment with dibutyltin dilaurate as the catalyst. In this article, we illustrated the physical behaviors were obviously influenced by synthetic routes. And their chemical and physical structures were investigated by gel permeation chromatograph (GPC), differential scanning calorimeter (DSC), fourier transform infrared spectrography (FT-IR) and mechanical properties tests. The surface wettability were studied by contact angle measurement (CA). As a kind of short-term implant biomaterial, the results of the hemolysis and platelet adhesive tests were recorded by spectrophotometer and scanning electron microscopy (SEM), indicating the materials have a great potential for developments and applications in biomedical field.