Carbazole-Equipped Metal-Organic Framework for Stability, Photocatalysis, and Fluorescence Detection.

The useful yet underutilized backfolded design is invoked here for functionalizing porous solids with the versatile carbazole function. Specifically, we attach carbazole groups as backfolded side arms onto the backbone of a linear dicarboxyl linker molecule. The bulky carbazole side arms point away from the carboxyl links and do not disrupt the Zr-carboxyl framework formation; namely, the resultant MOF solid ZrL1 features the same net as that of the unfunctionalized dicarboxyl linker, also known as the PCN-111 net or UiO-66 net. The ZrL1 structure features only half linker occupancy (about 6 out of the 12 linkers around the Zr6O8 cluster being missing) and partially collapses upon activation (acetone exchange and evacuation). Notably, the stability improves after heating in diphenyl oxide at 260 °C (POP-260 treatment; to form ZrL1-260), as indicated by the higher crystallinity and surface area of the activated ZrL1-260 sample. The ZrL1-260 samples achieve 72% yield in photocatalyzing reductive dehalogenation of phenacyl bromide; ZrL1 can detect nitro-aromatic compounds via fluorescence quenching, with selectivity and sensitivity toward 4-nitroaniline, featuring a limit of detection of 96 ppb.

A Ferrocene Metal-Organic Framework Solid for Fe-Loaded Carbon Matrices and Nanotubes: High-Yield Synthesis and Oxygen Reduction Electrocatalysis.

Using a carbon-rich designer metal-organic framework (MOF), we open a high-yield synthetic strategy for iron-nitrogen-doped carbon (Fe-N-C) nanotube materials that emulate the electrocatalysis performance of commercial Pt/C. The Zr(IV)-based MOF solid boasts multiple key functions: (1) a dense array of alkyne units over the backbone and the side arms, which are primed for extensive graphitization; (2) the open, branched structure helps maintain porosity for absorbing nitrogen dopants; and (3) ferrocene units on the side arms as atomically dispersed precursor catalyst for targeting micropores and for effective iron encapsulation in the carbonized product. As a result, upon pyrolysis, over 89% of the carbon component in the MOF scaffold is successfully converted into carbonized products, thereby contrasting the easily volatilized carbon of most MOFs. Moreover, over 97% of the iron ends up being encased as acid-resistant Fe/Fe3C nanoparticles in carbon nanotubes/carbon matrices.