ABSTRACT
The new, quaternary diamond-like semiconductor (DLS) Cu4MnGe2S7 was prepared at high-temperature from a stoichiometric reaction of the elements under vacuum. Single crystal X-ray diffraction data were used to solve and refine the structure in the polar space group Cc. Cu4MnGe2S7 features [Ge2S7]6- units and adopts the Cu5Si2S7 structure type that can be considered a derivative of the hexagonal diamond structure. The DLS Cu2MnGeS4 with the wurtz-stannite structure was similarly prepared at a lower temperature. The achievement of relatively phase-pure samples, confirmed by X-ray powder diffraction data, was nontrival as differential thermal analysis shows an incongruent melting behaviour for both compounds at relatively high temperature. The dark red Cu2MnGeS4 and Cu4MnGe2S7 compounds exhibit direct optical bandgaps of 2.21 and 1.98 eV, respectively. The infrared (IR) spectra indicate potentially wide windows of optical transparency up to 25 µm for both materials. Using the Kurtz-Perry powder method, the second-order nonlinear optical susceptibility, χ(2), values for Cu2MnGeS4 and Cu4MnGe2S7 were estimated to be 16.9 ± 2.0 pm V-1 and 2.33 ± 0.86 pm V-1, respectively, by comparing with an optical-quality standard reference material, AgGaSe2 (AGSe). Cu2MnGeS4 was found to be phase matchable at λ = 3100 nm, whereas Cu4MnGe2S7 was determined to be non-phase matchable at λ = 1600 nm. The weak SHG response of Cu4MnGe2S7 precluded phase-matching studies at longer wavelengths. The laser-induced damage threshold (LIDT) for Cu2MnGeS4 was estimated to be â¼0.1 GW cm-2 at λ = 1064 nm (pulse width: τ = 30 ps), while the LIDT for Cu4MnGe2S7 could not be ascertained due to its weak response. The significant variance in NLO properties can be reasoned using the results from electronic structure calculations.
ABSTRACT
Reductive carbonylation of TaCl(5) in the presence of 1,2-bis(diphenylphosphino)ethane (dppe) under the appropriate conditions results in the formation of TaCl(CO)(2)(dppe)(2) (1), as the major product, and the possibly cyclic oligomer [TaCl(CO)(2)(dppe)(2)](2)(x)() (2, 2x >/= 4) as a minor product. Carbonylation of 1 (1 atm) results in the rapid but reversible formation of TaCl(CO)(4)(dppe) (3). Solutions of all three compounds exhibit low levels of paramagnetism, possibly attributable to thermal population of low-lying triplet excited states. Crystal data for the toluene solvate of 1, C(68)H(64)ClO(2)P(4)Ta: triclinic, P&onemacr; (No. 2), a = 13.937(12) Å, b = 14.811(7) Å, c = 14.929(9) Å, alpha = 102.30(5) degrees, beta = 95.60(7) degrees, gamma = 98.41(5) degrees, Z = 2.
ABSTRACT
The effects of onion juice on several characteristics of cooked ground lamb were investigated. Onion juice was a more effective antioxidant than garlic juice in reducing development of rancidity in meat. TBA values for onion-treated samples were lower (P<0.05) after storage when the distillation method of TBA measurement was used. The extraction method may be a less sensitive test for rancidity. Taste panelists were able to discriminate between the onion-treated samples and the control, but onion samples were not preferred (P>.05). Mean hedonic scores were higher (P<0.05) for the onion-treated samples, indicating a more acceptable flavor after storage.