ABSTRACT
Dental implant failures caused by bacterial infections are a significant concern for dental implantologists. We modified the titanium surface by depositing silver (Ti-Ag) using direct current (DC) sputtering and confirmed the formation of a 'nano coat' by X-ray photoelectron spectroscopy (XPS), surface profilometry and energy dispersive spectroscopy (EDS). Scanning electron microscopy (SEM) and atomic force microscopy (AFM) revealed the deposition of a uniform nano Ag thin film. A gradual increase in thickness was observed, and the film thickness (530 nm) at 5 min deposition time (Ti-Ag5) resulted in a reduction of the water contact angle (WCA, 15%) and an increase in surface energy (SFE, 22%) in comparison to the uncoated Ti surface. Using inductively coupled plasma-atomic emission spectroscopy (ICP-AES), the slow, steady release of Ag from the coating was observed over 21 days. The Ti-Ag5 surface exhibited excellent antibacterial activity against Streptococcus oralis, Streptococcus sanguinis, Aggregatibacter actinomycetemcomitans, and Porphyromonas gingivalis, which belonged to the yellow, purple, and red complexes, representing specific periodontal pathogens. Furthermore, we observed excellent cytocompatibility of Ag-deposited Ti towards MG-63 osteoblasts with no inhibitory effect on their proliferative potential. Quantitation of alkaline phosphatase (ALP) activity, mineralization efficiency, and osteogenesis-related gene expression of MG-63 cells over 21 days was suggestive of rapid osseointegration. Overall, the 'nano coat' of Ag on Ti is indeed a prophylactic against peri-implantitis, ensuring increased implant success.
ABSTRACT
The clinical success of implants depends on rapid osseointegration, and new materials are being developed considering the increasing demand. Considering cobalt (Co) antibacterial characteristics, we developed Co-deposited titanium (Ti) using direct current (DC) sputtering and investigated it as a new material for implant dentistry. The material was characterized using atomic absorption spectroscopy, scanning electron microscopy-energy dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy. The material's surface topography, roughness, surface wettability, and hardness were also analyzed. The Co thin film (Ti-Co15) showed excellent antibacterial effects against microbes implicated in peri-implantitis. Furthermore, Ti-Co15 was compatible and favored the attachment and spreading of MG-63 cells. The alkaline phosphatase and calcium mineralization activities of MG-63 cells cultured on Ti-Co15 remained unaltered compared to Ti. These data correlated well with the time-dependent expression of ALP, RUNX-2, and BMP-2 genes involved in osteogenesis. The results demonstrate that Co-deposited Ti could be a promising material in implant dentistry.
ABSTRACT
The present study aimed to assess the efficacy of photofunctionalization on commercially available dental implant surfaces in a high-glucose environment. Discs of three commercially available implant surfaces were selected with various nano- and microstructural alterations (Group 1-laser-etched implant surface, Group 2-titanium-zirconium alloy surface, Group 3-air-abraded, large grit, acid-etched surface). They were subjected to photo-functionalization through UV irradiation for 60 and 90 min. X-ray photoelectron spectroscopy (XPS) was used to analyze the implant surface chemical composition before and after photo-functionalization. The growth and bioactivity of MG63 osteoblasts in the presence of photofunctionalized discs was assessed in cell culture medium containing elevated glucose concentration. The normal osteoblast morphology and spreading behavior were assessed under fluorescence and phase-contrast microscope. MTT (3-(4,5 Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) and alizarin red assay were performed to assess the osteoblastic cell viability and mineralization efficiency. Following photofunctionalization, all three implant groups exhibited a reduced carbon content, conversion of Ti4+ to Ti3+, increased osteoblastic adhesion, viability, and increased mineralization. The best osteoblastic adhesion in the medium with increased glucose was seen in Group 3. Photofunctionalization altered the implant surface chemistry by reducing the surface carbon content, probably rendering the surfaces more hydrophilic and conducive for osteoblastic adherence and subsequent mineralization in high-glucose environment.