A Functionally Graded PICN Material for Biomimetic CAD-CAM Blocks.

The objective of this study was to introduce a functionally graded (FG) polymer-infiltrated ceramic network (PICN) block, characterized by a gradient of mechanical properties, as a biomimetic material for computer-aided design and manufacturing (CAD-CAM) prostheses. FG-PICN blocks were manufactured from a slurry of glass-ceramic powder, which was subsequently centrifuged and sintered. The ceramic network was infiltrated with urethane dimethacrylate and polymerized under high temperature-pressure. Blocks were sectioned into 9 layers, and each layer was subsequently cut into 3 samples. Samples were loaded into a 3-point bending device and tested for flexural strength, flexural load energy, and flexural modulus. The volume percentage of glass-ceramic, hardness, and brittleness index were also measured and scanning electron microscopy (SEM) observations were performed. Katana translucent zirconia (HT-ZIR) and e.max-CAD (EMX) were tested for comparison. Flexural strength, flexural load energy, and Weibull modulus of FG-PICN were shown to increase from the first (enamel-like zone) to the ninth layer (dentin-like zone), while, on the contrary, flexural modulus, hardness, brittleness index, and ceramic volume percentage decreased. SEM characterization highlighted a higher porosity in layer 9 than in layer 1. Flexural strength of the dentin-like zone (372.7 ± 27.8 MPa) was similar to EMX and lower than HT-ZIR. Flexural modulus was shown to vary from 41.9 ± 5.1 to 28.6 ± 2.0 GPa from surface to depth. Flexural load energy in the dentin-like zone (27.1 ± 4.9 mJ) was significantly superior to EMX and HT-ZIR. Hardness gradient was shown to be close to tooth tissues. This work introduces FG-PICN blocks, with a gradient of mechanical and optical properties through the entire thickness of the block designed to mimic dental tissues. FG-PICN demonstrated a favorable gradient of flexural strength, elastic modulus, and, most of all, flexural load energy and hardness compared to other CAD-CAM materials, which can promote the biomechanical behavior of single-unit restorations on teeth and implants.

Wear measurement of dental tissues and materials in clinical studies: A systematic review.

OBJECTIVES: This study aims to systematically review the different methods used for wear measurement of dental tissues and materials in clinical studies, their relevance and reliability in terms of accuracy and precision, and the performance of the different steps of the workflow taken independently. METHODS: An exhaustive search of clinical studies related to wear of dental tissues and materials reporting a quantitative measurement method was conducted. MedLine, Embase, Scopus, Cochrane Library and Web of Science databases were used. Prospective studies, pilot studies and case series (>10 patients), as long as they contained a description of wear measurement methodology. Only studies published after 1995 were considered. RESULTS: After duplicates' removal, 495 studies were identified, and 41 remained for quantitative analysis. Thirty-four described wear-measurement protocols, using digital profilometry and superimposition, whereas 7 used alternative protocols. A specific form was designed to analyze the risk of bias. The methods were described in terms of material analyzed; study design; device used for surface acquisition; matching software details and settings; type of analysis (vertical height-loss measurement vs volume loss measurement); type of area investigated (entire occlusal area or selective areas); and results. SINIFICANCE: There is a need of standardization of clinical wear measurement. Current methods exhibit accuracy, which is not sufficient to monitor wear of restorative materials and tooth tissues. Their performance could be improved, notably limiting the use of replicas, using standardized calibration procedures and positive controls, optimizing the settings of scanners and matching softwares, and taking into account unusable data.

Bonding to CAD-CAM Composites: An Interfacial Fracture Toughness Approach.

The objective of this study was to evaluate the interfacial fracture toughness (IFT) of composite cement with dispersed filler (DF) versus polymer-infiltrated ceramic network (PICN) computer-aided design and computer-aided manufacturing (CAD-CAM) composite blocks after 2 different surface pretreatments using the notchless triangular prism (NTP) test. Two DFs (Cerasmart [CRT] and Lava Ultimate [LVA]), 2 PICNs (Enamic [ENA] and experimental PICN [EXP]), and e.max CAD lithium disilicate glass-ceramic (EMX, control) prism samples were bonded to their counterparts with Variolink Esthetic DC composite cement after either hydrofluoric acid etching (HF) or gritblasting (GR). Both procedures were followed by silanization. All samples ( n = 30 per group) were thermocycled (10,000 cycles) and tested for their IFT in a water bath at 36°C. Moreover, representative samples from each group were subjected to a developed interfacial area ratio (Sdr) measurement by profilometry and scanning electron microscopy (SEM) characterization. EXP-HF gave the highest IFT (1.85 ± 0.39 MPa·m1/2), followed by EMX-HF and ENA-HF, while CRT-HF gave the lowest (0.15 ± 0.22 MPa·m1/2). PICNs gave significantly better results with HF, and DF showed better results with GR. A 2-way analysis of variance indicated that there were significantly higher IFT and Sdr for PICNs than for DF. A positive correlation ( r² = 0.872) was found between IFT and Sdr. SEM characterization showed the specific microstructure of the surface of etched PICNs, indicating the presence of a retentive polymer-based honeycomb structure. Etching of the typical double-network microstructure of PICNs causes an important increase in the Sdr and IFT, while DF should be gritblasted. DF exhibited significantly lower Sdr and IFT values than PICNs. The present results show the important influence of the material class and surface texture, and consequently the micromechanical bond, on the adhesive interface performance of CAD-CAM composites.

From Artisanal to CAD-CAM Blocks: State of the Art of Indirect Composites.

Indirect composites have been undergoing an impressive evolution over the last few years. Specifically, recent developments in computer-aided design-computer-aided manufacturing (CAD-CAM) blocks have been associated with new polymerization modes, innovative microstructures, and different compositions. All these recent breakthroughs have introduced important gaps among the properties of the different materials. This critical state-of-the-art review analyzes the strengths and weaknesses of the different varieties of CAD-CAM composite materials, especially as compared with direct and artisanal indirect composites. Indeed, new polymerization modes used for CAD-CAM blocks-especially high temperature (HT) and, most of all, high temperature-high pressure (HT-HP)-are shown to significantly increase the degree of conversion in comparison with light-cured composites. Industrial processes also allow for the augmentation of the filler content and for the realization of more homogeneous structures with fewer flaws. In addition, due to their increased degree of conversion and their different monomer composition, some CAD-CAM blocks are more advantageous in terms of toxicity and monomer release. Finally, materials with a polymer-infiltrated ceramic network (PICN) microstructure exhibit higher flexural strength and a more favorable elasticity modulus than materials with a dispersed filler microstructure. Consequently, some high-performance composite CAD-CAM blocks-particularly experimental PICNs-can now rival glass-ceramics, such as lithium-disilicate glass-ceramics, for use as bonded partial restorations and crowns on natural teeth and implants. Being able to be manufactured in very low thicknesses, they offer the possibility of developing innovative minimally invasive treatment strategies, such as "no prep" treatment of worn dentition. Current issues are related to the study of bonding and wear properties of the different varieties of CAD-CAM composites. There is also a crucial need to conduct clinical studies. Last, manufacturers should provide more complete information regarding their product polymerization process, microstructure, and composition, which significantly influence CAD-CAM material properties.

Residual stress profiles in veneering ceramic on Y-TZP, alumina and ZTA frameworks: measurement by hole-drilling.

OBJECTIVES: The residual stress profile developed within the veneering ceramic during the manufacturing process is an important predicting factor in chipping failures, which constitute a well-known problem with yttria-tetragonal-zirconia polycrystal (Y-TZP) based restorations. The objectives of this study are to measure and to compare the residual stress profile in the veneering ceramic layered on three different polycrystalline ceramic framework materials: Y-TZP, alumina polycrystal (AL) and zirconia toughened alumina (ZTA). METHODS: The stress profile was measured with the hole-drilling method in bilayered disk samples of 19 mm diameter with a 0.7 mm thick Y-TZP, AL or ZTA framework and a 1.5mm thick layer of the corresponding veneering ceramic. RESULTS: The AL samples exhibited increasing compressive stresses with depth, while compressive stresses switching into interior tensile stresses were measured in Y-TZP samples. ZTA samples exhibited compressive stress at the ceramic surface, decreasing with depth up to 0.6mm from the surface, and then becoming compressive again near the framework. SIGNIFICANCE: Y-TZP samples exhibited a less favorable stress profile than those of AL and ZTA samples. Results support the hypothesis of the occurrence of structural changes within the Y-TZP surface in contact with the veneering ceramic to explain the presence of tensile stresses. Even if the presence of Y-TZP in the alumina matrix seems to negatively affect the residual stress profiles in ZTA samples in comparison with AL samples, the registered profiles remain positive in terms of veneer fracture resistance.