In vivo effect of UV-photofunctionalization of CoCrMo in processes of guided bone regeneration and tissue engineering.

Photofunctionalization of implant materials with ultraviolet (UV) radiation have been subject of study in the last two decades, and previous research on CoCrMo discs have showed good results in terms of bioactivity and the findings of apatite-like crystals in vitro. In the current study, CoCrMo domes were photofunctionalized with UV radiation of 254 nm on their internal faces during 24 hr; they were implanted in rabbit tibia and remained for 3, 4, and 6 weeks. The potential to induce bone formation beneath the dome-shaped membranes was evaluated through morphometric, histologic, and density measurements; and the results were compared with those obtained under control untreated domes. Higher density values were observed for irradiated domes at 3 weeks, whereas higher volumes were obtained under photofunctionalized domes for longer periods (4 and 6 weeks). Histologically, woven bone was formed by endochondral ossification in all cases; differences in the architecture and size of the trabeculae and in the number of osteoblasts were noted between irradiated and non-irradiated samples. The UV radiation of 254 nm generated a larger bone volume fraction compared to that found in the absence of UVC radiation and induced an increase of density in the early stages of healing, leading to a better initial bone quality and improved osseointegration.

Influence of Chromium-Cobalt-Molybdenum Alloy (ASTM F75) on Bone Ingrowth in an Experimental Animal Model.

Cr-Co-Mo (ASTM F75) alloy has been used in the medical environment, but its use as a rigid barrier membrane for supporting bone augmentation therapies has not been extensively investigated. In the present study, Cr-Co-Mo membranes of different heights were placed in New Zealand white, male rabbit tibiae to assess the quality and volume of new bone formation, without the use of additional factors. Animals were euthanized at 20, 30, 40, and 60 days. Bone formation was observed in all of the cases, although the tibiae implanted with the standard membranes reached an augmentation of bone volume that agreed with the density values over the timecourse. In all cases, plasmatic exudate was found under the membrane and in contact with the new bone. Histological analysis indicated the presence of a large number of chondroblasts adjacent to the inner membrane surface in the first stages, and osteoblasts and osteocytes were observed under them. The bone formation was appositional. The Cr-Co-Mo alloy provides a scaffold with an adequate microenvironment for vertical bone volume augmentation, and the physical dimensions and disposition of the membrane itself influence the new bone formation.