ABSTRACT
In this study, for the first time, a composite fluff pulp was produced based on the combination of softwood (i.e., long-length fiber), hardwood (i.e., short-length fiber), non-wooden pulps (i.e., bagasse) and bentonite, with specific amounts to be used in hygienic pads (e.g., baby diapers and sanitary napkins). After the defibration process, the manufactured fluff pulp was placed as an absorbent mass in diapers and sanitary napkins. Therefore, tests related to the fluff pulp, such as grammage, thickness, density, ash content, humidity percentage, pH and brightness, tests related to the manufactured baby diapers, such as absorption capacity, retention rate, retention capacity, absorption time and rewet, and tests related to the sanitary napkin, such as absorption capacity and rewet, were performed according to the related standards. The results demonstrated that increasing the amount of bagasse pulp led to increasing the ash content, pH and density of fluff pulp and decreasing the brightness. The addition of bentonite as a filler also increased ash content and pH of fluff pulp. The results also demonstrated that increasing of bagasse pulp up to 30% in combination with softwood pulp led to increasing absorption capacity, retention rate, retention capacity, absorption time and rewet of baby diapers and of sanitary napkins.
Subject(s)
Bentonite , Skin , Humans , Industry , InfantABSTRACT
The aim of this work is to investigate the effect of the fortification level of nanowollastonite on urea-formaldehyde resin (UF) and its effect on mechanical and physical properties of oriented strand lumbers (OSL). Two resin contents are applied, namely, 8% and 10%. Nanowollastonite is mixed with the resin at two levels (10% and 20%). It is found that the fortification of UF resin with 10% nanowollastonite can be considered as an optimum level. When nanowollastonite content is higher (that is, 20%), higher volume of UF resin is left over from the process of sticking the strips together, and therefore is absorbed by wollastonite nanofibers. The mechanism involved in the fortification of UF resin with nanowollastonite, which results in an improvement of thickness swelling values, can be attributed to the following two main factors: (i) nanowollastonite compounds making active bonds with the cellulose hydroxyl groups, putting them out of reach for bonding with the water molecules and (ii) high thermal conductivity coefficient of wollastonite improving the transfer of heat to different layers of the OSL mat, facilitating better and more complete resin curing. Since nanowollastonite contributes to making bonds between the wood strips, which consequently improves physical and mechanical properties, its use can be safely recommended in the OSL production process to improve the physical and mechanical properties of the panel.