ABSTRACT
Cyclodextrin (CD)-based polymers are known to efficiently form molecular inclusion complexes with various organic and inorganic guest compounds. In addition, they also have a great potential as metal complexes because deprotonated hydroxyls can strongly bind metal ions under alkaline conditions. The range of environmental conditions for polycyclodextrin/metal ion complexation can be extended by the polymerization of CDs with polyacids. This article describes the preparation and characterization of a new type of poly(ß-cyclodextrin) (Poly-ßCD) sub-micrometric fibers and explores their potential as metal ion sorbents. A water-soluble hyper-branched ß-cyclodextrin polymer was blended with poly(vinyl alcohol) (PVA) and here used to improve the mechanical and morphological features of the fibers. Solutions with a different Poly-ßCD/PVA ratio were electrospun, and the fibers were cross-linked by a post-spinning thermal treatment at 160 °C to ensure non-solubility in water. The fiber morphology was analyzed by scanning electron microscopy (SEM) before and after the curing process, and physical-chemical properties were studied by Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The capability of the insoluble cyclodextrin-based fibers to remove heavy metals from wastewaters was investigated by testing the adsorption of Cu2+ and Cd2+ using inductively coupled plasma-optical emission spectroscopy (ICP-OES). The results suggest that the poly(ß-cyclodextrin)/poly(vinyl alcohol) sub-micrometric fibers can complex metal ions and are especially effective Cu2+ sorbents, thus opening new perspectives to the development of fibers and membranes capable of removing both metal ions and organic pollutants.
ABSTRACT
The effect of plasticizer species and the degree of hydrolysis (DH) on the free volume properties of poly(vinyl alcohol) (PVA) were studied using positron annihilation lifetime spectroscopy. Both glycerol and propylene glycol caused an increase in the free volume cavity radius, although exhibited distinct plasticization behavior, with glycerol capable of occupying existing free volume cavities in the PVA to some extent. The influence of water, normally present in PVA film under atmospheric conditions, was also isolated. Water added significantly to the measured free volume cavity radius in both plasticized and pure PVA matrices. Differences in plasticization behavior can be attributed to the functionality of each plasticizing additive and its hydrogen bonding capability. The increase in cavity radii upon plasticizer loading shows a qualitative link between the free volume of voids and the corresponding reduction in Tg and crystallinity. Cavity radius decreases with increasing DH, due to PVA network tightening in the absence of acetate groups. This corresponds well with the higher Tg observed in the resin with the higher DH. DH was also shown to impact the plasticization of PVA with glycerol, indicating that the larger cavities-created by the weaker hydrogen bonding acetate groups-are capable of accommodating glycerol molecules with negligible effect on the cavity dimensions.
ABSTRACT
A missing cornerstone in the development of tough micro/nano fibre systems is an understanding of the fibre failure mechanisms, which stems from the limitation in observing the fracture of objects with dimensions one hundredth of the width of a hair strand. Tensile testing in the electron microscope is herein adopted to reveal the fracture behaviour of a novel type of toughened electrospun poly(methyl methacrylate)/poly(ethylene oxide) fibre mats for biomedical applications. These fibres showed a toughness more than two orders of magnitude greater than that of pristine PMMA fibres. The in-situ microscopy revealed that the toughness were not only dependent on the initial molecular alignment after spinning, but also on the polymer formulation that could promote further molecular orientation during the formation of micro/nano-necking. The true fibre strength was greater than 150â MPa, which was considerably higher than that of the unmodified PMMA (17â MPa). This necking phenomenon was prohibited by high aspect ratio cellulose nanocrystal fillers in the ultra-tough fibres, leading to a decrease in toughness by more than one order of magnitude. The reported necking mechanism may have broad implications also within more traditional melt-spinning research.
ABSTRACT
A new type of antimicrobial, biocompatible and toughness enhanced ultra-thin fiber mats for biomedical applications is presented. The tough and porous fiber mats were obtained by electrospinning solution-blended poly (methyl methacrylate) (PMMA) and polyethylene oxide (PEO), filled with up to 25 wt % of Lanasol--a naturally occurring brominated cyclic compound that can be extracted from red sea algae. Antibacterial effectiveness was tested following the industrial Standard JIS L 1902 and under agitated medium (ASTM E2149). Even at the lowest concentrations of Lanasol, 4 wt %, a significant bactericidal effect was seen with a 4-log (99.99%) reduction in bacterial viability against S. aureus, which is one of the leading causes of hospital-acquired (nosocomial) infections in the world. The mechanical fiber toughness was insignificantly altered up to the maximum Lanasol concentration tested, and was for all fiber mats orders of magnitudes higher than electrospun fibers based on solely PMMA. This antimicrobial fiber system, relying on a dissolved antimicrobial agent (demonstrated by X-ray diffraction and Infrared (IR)-spectroscopy) rather than a dispersed and "mixed-in" solid antibacterial particle phase, presents a new concept which opens the door to tougher, stronger and more ductile antimicrobial fibers.