ABSTRACT
Iron-manganese (Fe-Mn) based degradable biomaterials have been proven as a suitable substitute to permanent internal fracture-fixation devices. However, lower degradation and bacterial infection are still major concerns. To overcome these limitations, in this work, we have incorporated copper (Cu) in Fe-Mn system. The objective is to produce Cu nano-precipitates and refined microstructure through suitable combination of cold-rolling and age-treatment, so that degradation is improved eventually. High resolution transmission electron microscope (TEM) and scanning transmission electron microscope (STEM) confirmed the Cu rich composition of the nano-precipitates. Number of precipitates increased as aging time increased. Three-dimensional visualization of Fe, Mn and Cu atomic distributions using atom probe tomography (APT), indicated that Cu precipitates were in 15-50 nm range. Large number of nano-precipitates along with lower dislocation density led to highest strength (1078 MPa) and ductility (37 %) for the 6 h age-treated sample. On the other hand, nano-precipitates and refined microstructure resulted highest degradation for the 12 h of age treated sample (0.091 mmpy). When E.Coli bacteria was cultured with the sample extract, significantly higher antibacterial efficacy was observed for the sample having higher nano-precipitates. Higher degradation rate did not cause cyto-toxicity, rather promoted statistically higher cell proliferation (1.5 times within 24 h) in in vitro cell-material interaction studies. In vivo biocompatibility of the alloy containing large nano-precipitates was confirmed from higher new bone regeneration (60%) in rabbit femur model. Overall study suggested that the optimization of the thermo-mechanical processes can effectively tailor the Fe-Mn-Cu alloys for successful internal fracture fixation. STATEMENT OF SIGNIFICANCE: In the present work, we have reported a noble thermo-mechanical approach to simultaneously achieve Cu nano-precipitates and grain refinement in Fe-20Mn-3Cu alloy.