ABSTRACT
Sonochemical synthesis can be a facile, fast, efficient, versatile and economical way to prepare a large variety of conventional or novel nanostructured materials (metallic, magnetic, semiconducting, polymeric, etc.). In this work, zinc oxide nanocrystals were synthesized by irradiating and heating at 90 °C in a commercial ultrasonic bath a water solution of zinc nitrate hexahydrate and ammonia solution or hexamethylenetetramine as base catalysts. The evolution of the powder morphology and its crystalline structure were investigated at different times of ultrasonic irradiation (0-9â hours) and compared with those of samples obtained by only heating the solutions in a muffle furnace in order to enlighten the growth mechanism. It resulted that: i) the crystal morphology depends on the selected base, ii) for samples obtained by using ultrasounds, the homogeneity of the powders depends on the irradiation time, iii) by comparing all samples obtained at 7â hours of heating, the aspect ratio of the crystals is higher for those that also underwent to ultrasounds.
ABSTRACT
Zinc oxide (ZnO) is one of the main functional materials used to realize chemiresistive gas sensors. In addition, ZnO can be grown through many different methods obtaining the widest family of unique morphologies. However, the relationship between the ZnO morphologies and their gas sensing properties needs more detailed investigations, also with the aim to improve the sensor performances. In this work, seven nanoforms (such as leaves, bisphenoids, flowers, needles, etc.) were prepared through simple wet chemical synthesis. Morphological and structural characterizations were performed to figure out their growth mechanisms. Then, the obtained powders were deposited through screen-printing technique to realize thick film gas sensors. The gas sensing behavior was tested toward some traditional target gases and some volatile organic compounds (acetone, acetaldehyde, etc.) and compared with ZnO morphologies. Results showed a direct correlation between the sensors responses and the powders features (morphology and size), which depend on the specific synthesis process. The sensors can be divided in two behavioral classes, following the two main morphology kinds: aggregates of nanocrystals (leaves and bisphenoids), exhibiting best performances versus all tested gases and monocrystal based (stars, needle, long needles, flowers, and prisms).
ABSTRACT
The proper operation of a fluid power system in terms of efficiency and reliability is directly related to the fluid state; therefore, the monitoring of fluid ageing in real time is fundamental to prevent machine failures. For this aim, an innovative methodology based on fluid vapor analysis through metal oxide (shortened: MOX) gas sensors has been developed. Two apparatuses were designed and realized: (i) A dedicated test bench to fast-age the fluid under controlled conditions; (ii) a laboratory MOX sensor system to test the headspace of the aged fluid samples. To prepare the set of MOX gas sensors suitable to detect the analytes' concentrations in the fluid headspace, different functional materials were synthesized in the form of nanopowders, characterizing them by electron microscopy and X-ray diffraction. The powders were deposited through screen-printing technology, realizing thick-film gas sensors on which dynamical responses in the presence of the fluid headspace were obtained. It resulted that gas sensors based on solid solution TixSn1-xO2 with x = 0.9 and 0.5 offered the best responses toward the fluid headspace with lower response and recovery times. Furthermore, a decrease in the responses (for all sensors) with fluid ageing was observed.