ABSTRACT
Samples of nickel cobaltite, a mixed oxide occurring in the spinel structure which is currently extensively investigated because of its prospective application as ferromagnetic, electrocatalytic, and cost-effective energy storage material were prepared in the form of nanocrystals stabilized in a highly porous silica aerogel and as unsupported nanoparticles. Nickel cobaltite nanocrystals with average size 4 nm are successfully grown for the first time into the silica aerogel provided that a controlled oxidation of the metal precursor phases is carried out, consisting in a reduction under H2 flow followed by mild oxidation in air. The investigation of the average oxidation state of the cations and of their distribution between the sites within the spinel structure, which is commonly described assuming the Ni cations are only located in the octahedral sites, has been carried out by X-ray absorption spectroscopy providing evidence for the first time that the unsupported nickel cobaltite sample has a Ni : Co molar ratio higher than the nominal ratio of 1 : 2 and a larger than expected average overall oxidation state of the cobalt and nickel cations. This is achieved retaining the spinel structure, which accommodates vacancies to counterbalance the variation in oxidation state.
ABSTRACT
Copper-based nanoparticles, supported on either a silica aerogel or cubic mesostructured silicas obtained by using two different synthetic protocols, were used as catalysts for the water gas shift reaction. The obtained nanocomposites were thoroughly characterised before and after catalysis through nitrogen adsorption-desorption measurements at -196 °C, TEM, and wide- and low-angle XRD. The samples before catalysis contained nanoparticles of copper oxides (either CuO or Cu2 O), whereas the formation of metallic copper nanoparticles, constituting the active catalytic phase, was observed either by using pre-treatment in a reducing atmosphere or directly during the catalytic reaction owing to the presence of carbon monoxide. A key role in determining the catalytic performances of the samples is played by the ability of different matrices to promote a high dispersion of copper metal nanoparticles. The best catalytic performances are obtained with the aerogel sample, which also exhibits constant carbon monoxide conversion values at constant temperature and reproducible behaviour after subsequent catalytic runs. On the other hand, in the catalysts based on cubic mesostructured silica, the detrimental effects related to sintering of copper nanoparticles are avoided only on the silica support, which is able to produce a reasonable dispersion of the copper nanophase.