ABSTRACT
This study characterizes the mechanical performance of the AlSi10Mg alloy produced by powder bed fusion-laser beam (PBF-LB) subjected to two combined cycles consisting of multilayer coating deposition (electroless nickel (Ni-P) + diamond-like carbon (DLC)) and heat treatment. In particular, the DLC deposition phase replaces the artificial aging step in the T5 and T6 heat treatments, obtaining the following post-production cycles: (i) Ni-P + DLC deposition and (ii) rapid solution (SHTR) (10 min at 510 °C) before Ni-P + DLC deposition. Microstructural characterization shows no appreciable modifications in the morphology and dimensions of the hard Si-rich phase of the eutectic network and secondary spheroidal Si phase. However, overaging phenomena induced by DLC coating deposition and differences in elastic-plastic properties between the multilayer coating and the PBF-LB AlSi10Mg substrate lead to a reduction in tensile strength by up to 31% and a significant decrease in ductility by up to 58%. In contrast, higher resistance to crack opening thanks to improved surface hardness and residual compressive stresses of the coating and reduced defect sensitivity of the substrate increase the fatigue resistance by 54% in T5-coated alloy and 24% in T6R-coated alloy. Moreover, the coating remains well adherent to the substrate during fatigue testing, not becoming a source of fatigue cracks.
ABSTRACT
Few systematic studies on the correlation between alloy microstructure and mechanical failure of the AlSi10Mg alloy produced by laser-based powder bed fusion (L-PBF) are available in the literature. This work investigates the fracture mechanisms of the L-PBF AlSi10Mg alloy in as-built (AB) condition and after three different heat treatments (T5 (4 h at 160 °C), standard T6 (T6B) (1 h at 540 °C followed by 4 h at 160 °C), and rapid T6 (T6R) (10 min at 510 °C followed by 6 h at 160 °C)). In-situ tensile tests were conducted with scanning electron microscopy combined with electron backscattering diffraction. In all samples the crack nucleation was at defects. In AB and T5, the interconnected Si network fostered damage at low strain due to the formation of voids and the fragmentation of the Si phase. T6 heat treatment (T6B and T6R) formed a discrete globular Si morphology with less stress concentration, which delayed the void nucleation and growth in the Al matrix. The analysis empirically confirmed the higher ductility of the T6 microstructure than that of the AB and T5, highlighting the positive effects on the mechanical performance of the more homogeneous distribution of finer Si particles in T6R.
ABSTRACT
The San Carlo Colossus, known as San Carlone, is a monument constituted by an internal stone pillar support to which a wrought iron structure is attached. Embossed copper sheets are fixed to the iron structure to give the final shape to the monument. After more than 300 years of outdoor exposure, this statue represents an opportunity for an in-depth investigation of long-term galvanic coupling between wrought iron and copper. Most iron elements of the San Carlone appeared in good conservation conditions with scarce evidence of galvanic corrosion. In some cases, the same iron bars presented some portions in good conservation conditions and other nearby portions with active corrosion. The aim of the present study was to investigate the possible factors correlated with such mild galvanic corrosion of wrought iron elements despite the widespread direct contact with copper for more than 300 years. Optical and electronic microscopy and compositional analyses were carried out on representative samples. Furthermore, polarisation resistance measurements were performed both on-site and in a laboratory. The results revealed that the iron bulk composition showed a ferritic microstructure with coarse grains. On the other hand, the surface corrosion products were mainly composed of goethite and lepidocrocite. Electrochemical analyses showed good corrosion resistance of both the bulk and surface of the wrought iron, and galvanic corrosion is not occurring probably due to the iron's relatively noble corrosion potential. The few areas where iron corrosion was observed are apparently related to environmental factors, such as the presence of thick deposits and to the presence of hygroscopic deposits that create localized microclimatic conditions on the surface of the monument.
ABSTRACT
Epilithic bacteria play a fundamental role in the conservation of cultural heritage (CH) materials. On stones, bacterial communities cause both degradation and bioprotection actions. Bronze biocorrosion in non-burial conditions is rarely studied. Only few studies have examined the relationship between bacteria communities and the chemical composition of patinas (surface degradation layers). A better comprehension of bacterial communities growing on our CH is fundamental not only to understand the related decay mechanisms but also to foresee possible shifts in their composition due to climate change. The present study aims at (1) characterizing bacterial communities on bronze and marble statues; (2) evaluating the differences in bacterial communities' composition and abundance occurring between different patina types on different statues; and (3) providing indications about a representative bacterial community which can be used in laboratory tests to better understand their influence on artefact decay. Chemical and biological characterization of different patinas were carried out by sampling bronze and marble statues in Bologna and Ravenna (Italy), using EDS/Raman spectroscopy and MinION-based 16SrRNA sequencing. Significant statistical differences were found in bacterial composition between marble and bronze statues, and among marble patinas in different statues and in the same statue. Marble surfaces showed high microbial diversity and were characterized mainly by Cyanobacteria, Proteobacteria and Deinococcus-Thermus. Bronze patinas showed low taxa diversity and were dominated by copper-resistant Proteobacteria. The copper biocidal effect is evident in greenish marble areas affected by the leaching of copper salts, where the bacterial community is absent. Here, Ca and Cu oxalates are present because of the biological reaction of living organisms to Cu ions, leading to metabolic product secretions, such as oxalic acid. Therefore, a better knowledge on the interaction between bacteria communities and patinas has been achieved.
Subject(s)
Calcium Carbonate , Copper , Artifacts , Bacteria , Calcium Carbonate/chemistry , Copper/chemistry , Oxalic Acid , SaltsABSTRACT
Plasma Electrolytic Oxidation (PEO) was applied to extruded ZM21 Mg alloys to improve their corrosion resistance in a chloride-containing environment. PEO was carried out in DC mode and voltage control in a fluoride-free electrolyte. Potentiodynamic polarization tests in 3.5 wt.% NaCl aqueous solution and neutral salt spray (NSS) tests were carried out. Microstructural and profilometric characterization, as well as NSS tests were performed in different conditions: (i) bare ZM21, (ii) PEO-treated ZM21, (iii) powder-coated ZM21 (without PEO interlayer), and (iv) PEO-treated ZM21 with powder coating top layer (carboxyl-functionalized polyester resin). The PEO + powder coating double layer was identified as the best-performing corrosion protection.
ABSTRACT
Recently, research gives emphasis to eco-friendly and sustainable approaches for the preservation of cultural heritage that could offer advantages in terms of compatibility, durability and safety. Hence, a biological treatment, based on a specific fungal strain of Beauveria bassiana, is exploited for the stabilization of soluble and/or active bronze corrosion products, converting them into copper oxalates. The chemical stability of the latter represents a real improvement for the long-term preservation of bronze, especially in case of exposure to acid rain. However, the corrosion behaviour of bronze differs from that of pure copper due to the presence of additional alloying elements. In natural environments, the selective dissolution of copper leads to a relative tin-enrichment within the corrosion layers, mostly in unsheltered areas exposed to rainwater runoff. To understand the influence of tin-enrichment on the formation of oxalates, pure tin and artificially tin-enriched bronze coupons were treated with this novel biological system and, in the case of bronze coupons, exposed to accelerated ageing. Tin enrichment and accelerated ageing were performed through runoff tests. Before and after treatment and ageing, the sample surface was characterized through Fourier transform infrared (FTIR) and Raman spectroscopies, scanning electron microscopy coupled to energy dispersive spectroscopy (SEM-EDS). Metals released in the ageing solutions were analysed through atomic absorption spectrometry (AAS). The analytical results allowed to better understand the response of unsheltered areas from outdoor bronze monuments to the biological treatment proposed.
Subject(s)
Corrosion , Tin , Alloys , Copper , Fungi , Metals , Microscopy, Electron, Scanning , Oxalates , Spectrometry, X-Ray Emission , Spectrophotometry, Atomic , Spectrum Analysis, RamanABSTRACT
Surface and building runoff can significantly contribute to the total metal loading in urban runoff waters, with potential adverse effects on the receiving ecosystems. The present paper analyses the corrosion-induced metal dissolution (Fe, Mn, Cr, Ni, Cu) from weathering steel (Cor-Ten A) with or without artificial patinas, exposed for 3 years in unsheltered conditions at a marine urban site (Rimini, Italy). The influence of environmental parameters, atmospheric pollutants and surface finish on the release of dissolved metals in rain was evaluated, also by means of multivariate analysis (two-way and three-way Principal Component Analysis). In addition, surface and cross-section investigations were performed so as to monitor the patina evolution. The contribution provided by weathering steel runoff to the dissolved Fe, Mn and Ni loading at local level is not negligible and pre-patination treatments seem to worsen the performance of weathering steel in term of metal release. Metal dissolution is strongly affected by extreme events and shows seasonal variations, with different influence of seasonal parameters on the behaviour of bare or artificially patinated steel, suggesting that climate changes could significantly influence metal release from this alloy. Therefore, it is essential to perform a long-term monitoring of the performance, the durability and the environmental impact of weathering steel.
Subject(s)
Rain , Soil Pollutants/analysis , Steel/analysis , Cities , Corrosion , Environmental Monitoring , Italy , Seasons , SolubilityABSTRACT
Rhizobia are important members of the soil microbiome since they enter into nitrogen-fixing symbiosis with different legume host plants. Rhizobium sp. LPU83 is an acid-tolerant Rhizobium strain featuring a broad-host-range. However, it is ineffective in nitrogen fixation. Here, the improved draft genome sequence of this strain is reported. Genome sequence information provides the basis for analysis of its acid tolerance, symbiotic properties and taxonomic classification.
Subject(s)
Genome, Bacterial , Rhizobium/classification , Rhizobium/genetics , Acids/metabolism , High-Throughput Nucleotide Sequencing , Medicago sativa/microbiology , Molecular Sequence Data , Nitrogen Fixation , Rhizobium/metabolism , Symbiosis/geneticsABSTRACT
Alfalfa (Medicago sativa) is the most cultivated forage legume for cattle and animal feeding, occupying about 32 million hectares over the world. Management of the N2-fixing symbiosis of this plant to maximize crop production is therefore an important objective. A fundamental constraint to this aim emerges when a moderately low soil pH hampers the establishment of an effective symbiosis with indigenous and/or inoculated rhizobia. Besides the association of alfalfa with Ensifer (Sinorhizobium) meliloti, this legume is able to establish a symbiosis with Ensifer (Sinorhizobium) medicae and with less characterized types of rhizobia, such as the Oregon-like strains, Rhizobium sp. Or191 initially isolated in the USA, and the Rhizobium sp. LPU83 strain, from Argentina. These strains are acid-tolerant, highly competitive for acidic-soil-alfalfa nodulation, but inefficient for biological nitrogen fixation with alfalfa. These features position the Oregon-like rhizobia as strains of potential risk in agricultural soils compared with the efficient symbiont E. meliloti. Moreover, the collected genetic information has revealed that the genomic structure of these rhizobial isolates is complex in terms of sequence similarities shared with other rhizobia. Such a "patched" genetic composition has obviously imposed severe restrictions to the classical taxonomy of these rhizobia. In this work we summarize the accumulated knowledge about the Oregon-like rhizobia and present a phylogenetic analysis based on genome sequence data of Rhizobium sp. LPU83 obtained by a high-throughput sequencing on the Genome Sequencer FLX Titanium platform. The accessibility of the complete genomic sequence will release up more experimental possibilities since this information will then enable biochemical studies as well as proteomics and transcriptomics approaches.
Subject(s)
Genome, Bacterial , Genomics/methods , Rhizobium/genetics , Genetic Variation , Medicago sativa/microbiology , Nitrogen Fixation/genetics , Phylogeny , Plasmids/genetics , Rhizobium/classification , Rhizobium/metabolism , Sinorhizobium/genetics , Symbiosis/geneticsABSTRACT
We report a child with a de novo interstitial deletion, 46,XY, int del(9)(9q22.31-q31.2). Cytogenetic and molecular analysis defined the boundaries of the lost region, of paternal origin, from D9S1796 to D9S938. The clinical picture included macrocephaly, frontal bossing, bilateral epicanthus, down-slanted palpebral fissures, low-set ears, hypoplastic nostrils, micrognathia, scoliosis, right single palmar crease, small nails, slender fingers, bilaterally flexed 5th finger, delayed bone age, abnormal metacarpophalangeal pattern (MCPP) profile and sole pits. No major malformation was recorded. The deleted region includes, among others, the PTCH and ROR2 genes. Mutations of the former cause the nevoid basal cell carcinoma syndrome (NBCCS) while mutations in the ROR2 gene have been found both in Robinow syndrome and in brachydactyly type 1B (BDB1). As the patient shows some clinical manifestation of both syndromes, we conclude that phenotypic changes related to haploinsufficiency of PTCH and ROR2 are recognisable in our patient even at a young age and in the presence of the more complex phenotype due to the deletion's large size. Thus the efforts to identify the genes included in a deletion are worthy as they may result in better care of the patient as, in this case, monitoring the possible development of tumours associated with NBCCS.