Coaxial Monitoring of AISI 316L Thin Walls Fabricated by Direct Metal Laser Deposition.

Direct metal laser deposition (DMLD) is an additive manufacturing technique suitable for coating and repair, which has been gaining a growing interest in 3D manufacturing applications in recent years. However, its diffusion in the manufacturing industry is still limited due to technical challenges to be solved-both the sub-optimal quality of the final parts and the low repeatability of the process make the DMLD inadequate for high-value applications requiring high-performance standards. Thus, real-time monitoring and process control are indispensable requirements for improving the DMLD process. The aim of this study was the optimization of deposition strategies for the fabrication of thin walls in AISI 316L stainless steel. For this purpose, a coaxial monitoring system and image processing algorithms were employed to study the melt pool geometry. The comparison tests carried out highlighted how the region-based active contour algorithm used for image processing is more efficient and stable than others covered in the literature. The results allowed the identification of the best deposition strategy. Therefore, it is shown how this monitoring methodology proved to be suitable for designing and implementing the right building strategy for DMLD manufactured 3D components. A fast and stable image processing method was achieved, which can be considered for future closed-loop monitoring in real-time applications.

Ultrasonic Characterization of Components Manufactured by Direct Laser Metal Deposition.

Direct laser metal deposition (DLMD) is an innovative additive technology becoming of key importance in the field of repairing applications for industrial and aeronautical components. The performance of the repaired components is highly related to the intrinsic presence of defects, such as cracks, porosity, excess of dilution or debonding between clad and substrate. Usually, the quality of depositions is evaluated through destructive tests and microstructural analysis. Clearly, such methodologies are inapplicable in-process or on repaired components. The proposed work aims to evaluate the capability of ultrasonic techniques to perform the mechanical characterization of additive manufactured (AM) components. The tested specimens were manufactured by DLMD using a nickel-based superalloy deposited on an AISI 304 substrate. Ultrasonic goniometric immersion tests were performed in order to mechanical characterize the substrate and the new material obtained by AM process, consisting of the substrate and the deposition. Furthermore, the relationship was evaluated between the acoustic and the mechanical properties of the AM components and the deposition process parameters and the geometrical characteristics of multiclad depositions, respectively. Finally, the effectiveness of the proposed non-destructive experimental approach for the characterization of the created deposition anomalies has been investigated.