ABSTRACT
This work demonstrated the potential of CNC as a substitute for PEG as an additive in ultrafiltration membrane fabrication. Two sets of modified membranes were fabricated using the phase inversion technique, with polyethersulfone (PES) as the base polymer and 1-N-methyl-2 pyrrolidone (NMP) as the solvent. The first set was fabricated with 0.075 wt% CNC, while the second set was fabricated with 2 wt% PEG. All membranes were characterized using SEM, EDX, FTIR, and contact angle measurements. The SEM images were analyzed for surface characteristics using WSxM 5.0 Develop 9.1 software. The membranes were tested, characterized, and compared for their performance in treating both synthetic and real restaurant wastewater. Both membranes exhibited improved hydrophilicity, morphology, pore structure, and roughness. Both membranes also exhibited similar water flux for real and synthetic polluted water. However, the membrane prepared with CNC gave higher turbidity removal and COD removal when raw restaurant water was treated. The membrane compared well with the UF membrane containing 2 wt% PEG in terms of morphology and performance when synthetic turbid water and raw restaurant water were treated.
ABSTRACT
In this work, cellulose nanocrystals (CNC) derived from sawdust were successfully incorporated into a nanofiltration membrane produced by the interfacial polymerization of piperazine (PIP) and trimesoyl chloride (TMC). The characteristics of unmodified and CNC-modified membranes were investigated using scanning electron microscopy (SEM), Atomic Force Microscopy (AFM), zeta potential measurement, X-ray photoelectron spectroscopy (XPS), and contact angle measurement. The performance of the membranes in terms of nitrate removal and water flux was investigated using 60 mg/L of potassium nitrate solution in a dead-end test cell. The characteristics of the modified membrane revealed a more nodular structure, higher roughness, increased negative surface charge, and higher hydrophilicity than the pristine membrane, leading to nitrate rejection of 94%. In addition, the membrane gave an average water flux of 7.2 ± 1.8 L/m2/h/bar. This work implies that nanofiltration, a relatively low-pressure process compared to reverse osmosis, can be used for improved nitrate removal from drinking water using an NF membrane modified with sawdust-derived cellulose nanocrystals.
ABSTRACT
Cellulose nanocrystals (CNC) obtained from waste sawdust were used to modify the polyamide membrane fabricated by interfacial polymerization of m-phenylene-diamine (MPDA) and trimesoyl chloride (TMC). The efficiency of the modification with sawdust-derived CNC was investigated using zeta potential and X-ray photoelectron spectroscopy (XPS). The effect of the modification on membrane mechanical strength and stability in acidic and alkaline solutions was also investigated. Results revealed that the negative zeta potential decreased at a high pH and the isoelectric point shifted into the acidic range for both modified and unmodified membranes. However, the negative charges obtained on the surface of the modified membrane at a pH lower than 8 were higher than the pristine membrane, which is an indication of the successful membrane modification. The XPS result shows that the degree of crosslinking was lowered due to the presence of CNC. Enhanced stability in solution in all pH ranges and the increase in mechanical strength, as indicated by higher Young's modulus, maximum load, and tensile strength, confirmed the robustness of the modified membrane.