ABSTRACT
Coaxial wire-based laser metal deposition is a versatile and efficient additive process that can achieve a high deposition rate in the manufacturing of complex structures. In this paper, a three-beam coaxial wire system is studied, with particular attention given to the effects of the deposition direction and laser beam orientation on the resulting bead geometry symmetry. With the three-beam laser delivery, the laser spot pattern is not always symmetric with respect to the deposition direction. Single titanium beads are deposited in different directions and at varying deposition rates, and the bead profile is quantitatively scored for multiple symmetry measures. Through an analysis of variance, the deposition direction and deposition rate were found to be insignificant with respect to the resulting bead symmetry for the developed measures. The bead symmetry and geometry are important factors in determining if a build is free of critical defects, and in this study, it is shown that the three-beam coaxial wire deposition setup is a directionally independent process.
ABSTRACT
Coaxial wire-based laser metal deposition is a versatile and efficient additive process that can achieve a high deposition rate in the manufacturing of complex structures. In this paper, a three-beam coaxial wire system is studied, with particular attention to the effects of deposition height and laser defocusing on the resulting bead geometry. As the deposition standoff distance changes, so does the workpiece illumination proportion, which describes the ratio of energy going directly into the feedstock wire and into the substrate. Single titanium beads are deposited at varying defocus levels and deposition rates and the bead aspect ratio is measured and analyzed. Over the experimental settings, the defocusing level and deposition rate were found to have a significant effect on the resulting bead aspect ratio. As the defocusing level is increased away from the beam convergence plane, the spot size increases and the deposited track is wider and flatter. Process parameters can be used to tune the deposited material to a desired aspect ratio. In coaxial wire deposition, defocusing provides an adjustment mechanism to the distribution of heat between the wire and substrate and has an important impact on the resulting deposit.
ABSTRACT
In this study, laser-directed energy deposition was applied to build a Ti-rich ternary Ti-Ni-Cu shape-memory alloy onto a TiNi shape-memory alloy substrate to realize the joining of the multifunctional bi-metallic shape-memory alloy structure. The cost-effective Ti, Ni, and Cu elemental powder blend was used for raw materials. Various material characterization approaches were applied to reveal different material properties in two sections. The as-fabricated Ti-Ni-Cu alloy microstructure has the TiNi phase as the matrix with Ti2Ni secondary precipitates. The hardness shows no high values indicating that the major phase is not hard intermetallics. A bonding strength of 569.1 MPa was obtained by tensile testing, and digital image correlation reveals the different tensile responses of the two sections. Differential scanning calorimetry was used to measure the phase-transformation temperatures. The austenite finishing temperature of higher than 80 °C was measured for the Ti-Ni-Cu alloy section. For the TiNi substrate, the austenite finishing temperature was tested to be near 47 °C at the bottom and around 22 °C at the upper substrate region, which is due to the repeated laser scanning that acts as annealing on the substrate. Finally, the multiple shape-memory effect of two shape-memory alloy sides was tested and identified.