Influence of Al2O3 Nanoparticle Addition on a UV Cured Polyacrylate for 3D Inkjet Printing.

The brittleness of acrylic photopolymers, frequently used in 3D Inkjet printing, limits their utilization in structural applications. In this study, a process was developed for the production and characterization of an alumina-enhanced nanocomposite with improved mechanical properties for Inkjet printing. Ceramic nanoparticles with an average primary particle size (APPS) of 16 nm and 31 nm, which was assessed via high-resolution scanning electron microscopy (HRSEM), were functionalized with 3.43 and 5.59 mg/m² 3-(trimethoxysilyl)propyl methacrylate (MPS), respectively, while being ground in a ball mill. The suspensions of the modified fillers in a newly formulated acrylic mixture showed viscosities of 14 and 7 mPa∙s at the printing temperature of 60 °C. Ink-jetting tests were conducted successfully without clogging the printing nozzles. Tensile tests of casted specimens showed an improvement of the tensile strength and elongation at break in composites filled with 31 nm by 10.7% and 74.9%, respectively, relative to the unfilled polymer.

Fused Deposition Modeling of ABS-Barium Titanate Composites: A Simple Route towards Tailored Dielectric Devices.

A process for the development, characterization and correlation of composite materials for 3D printing is presented, alongside the processing of a polymer-ceramic functional composite using fused deposition modeling (FDM). The composite was developed using acrylonitrile butadiene styrene (ABS) as the matrix material filled with barium titanate (BT) micro-powder up to 35 vol % (74.2 wt %). The ABS-BT composites exhibited a shear thinning behavior with increasing ceramic content. The composite was 3D printed into structural and functional test samples using FDM by adapting and optimizing the print parameters. Structural characterization revealed increasingly brittle behavior at higher filler ratios, with the ultimate tensile strength falling from 25.5 MPa for pure ABS to 13.7 MPa for the ABS-35 vol % BT composite. Four-point flexural tests showed a similar decrease in flexural strength with increasing ceramic content. Functional characterization revealed an increase in the relative permittivity at 200 kHz from 3.08 for pure ABS to 11.5 for the composite with 35 vol % BT. These results were correlated with the Maxwell-Garnett and Jayasundere-Smith effective medium models. The process described in this work can be used for other 3D printing processes and provides a framework for the rapid prototyping of functional composites into functional parts with reliable properties. The ABS-BT composite shows promise as a functional dielectric material, with potential applications as capacitors and light-weight passive antennas.