Hydrothermal Synthesis of Silicoaluminophosphate with AEL Structure Using a Residue of Fluorescent Lamps as Starting Material.

Silicoaluminophosphate molecular sieves of SAPO-11 type (AEL structure) were synthesized by the hydrothermal method, from the residue of a fluorescent lamp as a source or Si, Al, and P in the presence of water and di-propyamine (DPA) as an organic template. To adjust the P2O5/SiO2 and Si/Al and ratios, specific amounts of silica, alumina, or alumina hydroxide and orthophosphoric acid were added to obtain a gel with molar chemical composition 1.0 Al2O3:1.0 P2O5:1.2 DPA:0.3 SiO2:120 H2O. The syntheses were carried out at a temperature of 473 K at crystallization times of 24, 48, and 72 h. The fluorescent lamp residue and the obtained samples were characterized by X-ray fluorescence, X-ray diffraction, scanning electron microscopy, and BET surface area analysis using nitrogen adsorption isotherms. The presence of fluorapatite was detected as the main crystalline phase in the residue, jointly with considered amounts of silica, alumina, and phosphorus in oxide forms. The SAPO-11 prepared using aluminum hydroxide as Al source, P2O5/SiO2 molar ratio of 3.6 and Si/Al ratio of 0.14, at crystallization time of 72 h, achieves a yield of 75% with a surface area of 113 m2/g, showing that the residue from a fluorescent lamp is an alternative source for development of new materials based on Si, Al, and P.

Memory Effect on a LDH/zeolite A Composite: An XRD In Situ Study.

In this memory effect study, hydrotalcite-type compounds in the lamellar double hydroxide-like (LDH)/zeolite A composite material were analyzed using X-Ray Diffration XRD) in situ experiments. Three samples were analyzed: Al,Mg-LDH, Al,Mg-LDH/ZA composite, and a physical mixture (50/50 wt%) of zeolite A and Al,Mg-LDH. The Al,Mg-LDH sample was treated at 500 °C in an O2 atmosphere and subsequently rehydrated. The Al,Mg-LDH/ZA composites had three treatments: one was performed at 300 °C in a He atmosphere, and two treatments were performed with an O2 atmosphere at 300 and 500 °C. In the physical mixture, two treatments were carried out under O2 flow at 500 °C and under He flow at 300 °C. Both went through the rehydration process. All samples were also analyzed by energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM). The results show that the LDH phase in the Al,Mg-LDH/ZA compounds has memory effects, and thus, the compound can be calcined and rehydrated. For the LDH in the composite, the best heat treatment system is a temperature of 300 °C in an inert atmosphere.