ABSTRACT
Precursor solution of CH3NH3PbI3-xClx for perovskite solar cells was conventionally prepared by mixing PbCl2 and CH3NH3I with a mole ratio of 1:3 (PbCl2:CH3NH3I). While in the present study, CH3NH3PbI3-xClx-based solar cells were fabricated using the precursor solutions containing PbCl2 and CH3NH3I with the mole ratios of 1:3, 1.05:3, 1.1:3, and 1.15:3, respectively. The results display that the solar cells with the mole ratio of 1.1:3 present higher power conversion efficiency and less I-V hysteresis than those with the mole ratio of 1:3. Based on some investigations, it is concluded that the higher efficiency could be due to the smooth and pinhole free film formation, high optical absorption, suitable energy band gap, and the large electron transfer efficiency, and the less I-V hysteresis may be attributed to the small low frequency capacitance of the device.
ABSTRACT
The present study reports Bi5FeTi3O15 (BFTO) nanofibers/graphene (Gr) nanocomposites (BGr) as counter electrodes (CEs) in dye-sensitized solar cells (DSSCs). BFTO nanofibers with diameters of 40-100 nm were fabricated by sol-gel based electrospinning technique. The microstructure and surface morphology of the BFTO nanofibers and the BGr nanocomposites were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The electrochemical performances of BGr CEs were comprehensively characterized and investigated. Compared to pristine BFTO, the nanocomposites have a marked improvement in electrocatalytic performance for the reduction of triiodide because of larger surface area and lower transfer resistance on the electrolyte-electrode interface. The maximum power conversion efficiency has reached 9.56%, which is much larger than that of pure BFTO CEs (0.22%).