ABSTRACT
This article presents an experimental study to analyze the mechanical properties of a soil stabilized with ordinary Portland cement (OPC) under a sustainable approach consisting of a significant substitution of OPC for sugarcane bagasse ash (SCBA) to reduce the quantity of cement used in the stabilization, reaching the necessary mechanical requirements for its use as a subgrade layer. Soil specimens were elaborated with 3%, 5%, and 7% OPC as a stabilizing agent by weight of the soil. These mixtures were then partially substituted with 25%, 50%, and 75% SCBA, with these percentages being by weight of the stabilizer (OPC). Compaction, compressive strength, and California bearing ratio (CBR) tests were performed to evaluate the mechanical properties of the specimens. The results indicate that a 25% substitution of OPC by SCBA shows a similar performance to the mixture with only Portland cement, so a reduction in OPC use can be made. Further, with a substitution of 100% OPC by SCBA, the CBR of natural soil without stabilizers is improved.
ABSTRACT
The use of supplementary cementitious materials such as fly ash, slag, and silica fume improve reinforced concrete corrosion performance, while decreasing cost and reducing environmental impact compared to ordinary Portland cement. In this study, the corrosion behavior of AISI 1018 carbon steel (CS) and AISI 304 stainless steel (SS) reinforcements was studied for 365 days. Three different concrete mixtures were tested: 100% CPC (composite Portland cement), 80% CPC and 20% silica fume (SF), and 80% CPC and 20% fly ash (FA). The concrete mixtures were designed according to the ACI 211.1 standard. The reinforced concrete specimens were immersed in a 3.5 wt.% NaCl test solution to simulate a marine environment. Corrosion monitoring was evaluated using the corrosion potential (Ecorr) according to ASTM C876 and the linear polarization resistance (LPR) according to ASTM G59. The results show that AISI 304 SS reinforcements yielded the best corrosion behavior, with Ecorr values mainly pertaining to the region of 10% probability of corrosion, and corrosion current density (icorr) values indicating passivity after 105 days of experimentation and low probability of corrosion for the remainder of the test period.