Determination of thermal properties and morphology of eucalyptus wood residue filled high density polyethylene composites.

Thermal behaviors of eucalyptus wood residue (EWR) filled recycled high density polyethylene (HDPE) composites have been measured applying the thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Morphology of the materials was also studied using scanning electron microscope (SEM). Addition of the EWR into the recycled HDPE matrix reduced the starting of degradation temperature. EWR filled recycled HDPE had two main decomposition peaks, one for EWR around 350 degrees C and one for recycled HDPE around 460 degrees C. Addition of EWR did not affect the melting temperature of the recycled HDPE. Morphological study showed that addition of coupling agent improved the compatibility between wood residue and recycled HDPE.

Some properties of composite panels made from wood flour and recycled polyethylene.

This study investigated the effect of board type (unmodified vs. MAPE modified) on the surface quality and thickness swelling-water absorption properties of recycled high density polyethylene (HDPE) based wood plastic composites. Additionally, two commercially available coatings (cellulosic coating and polyurethane lacquer coating) were also applied to composite surfaces and their adhesion strength, abrasion and scratch resistance, and gloss values were determined. This study showed that modification of the composites with MAPE coupling agent increased the surface smoothness and reduced the water absorption and thickness swelling of the panels. Abrasion resistance of the composites was also improved through MAPE modification. Regardless of board type, higher scratch resistance and gloss values were observed for polyurethane lacquer coated samples compared to those of cellulosic varnish coated ones. Improvement of adhesion strength was also seen on SEM micrographs.

Thermal Degradation, Mechanical Properties and Morphology of Wheat Straw Flour Filled Recycled Thermoplastic Composites.

Thermal behaviors of wheat straw flour (WF) filled thermoplastic compositeswere measured applying the thermogravimetric analysis and differential scanningcalorimetry. Morphology and mechanical properties were also studied using scanningelectron microscope and universal testing machine, respectively. Presence of WF inthermoplastic matrix reduced the degradation temperature of the composites. One for WFand one for thermoplastics, two main decomposition peaks were observed. Morphologicalstudy showed that addition of coupling agent improved the compatibility between WFs andthermoplastic. WFs were embedded into the thermoplastic matrix indicating improvedadhesion. However, the bonding was not perfect because some debonding can also be seenon the interface of WFs and thermoplastic matrix. In the case of mechanical properties ofWF filled recycled thermoplastic, HDPE and PP based composites provided similar tensileand flexural properties. The addition of coupling agents improved the properties ofthermoplastic composites. MAPE coupling agents performed better in HDPE while MAPPcoupling agents were superior in PP based composites. The composites produced with thecombination of 50-percent mixture of recycled HDPE and PP performed similar with theuse of both coupling agents. All produced composites provided flexural properties requiredby the ASTM standard for polyolefin-based plastic lumber decking boards.