ABSTRACT
This work is within the objective of understanding the effects caused to Fe-Cr alloys by fast Fe ion irradiation. As the penetration length of Fe ion is of the order of hundreds of nanometers, 70 nm Fe-5at%C and Fe-10at%Cr films were irradiated at room temperature with 490 keV Fe+ ions at increasing fluence corresponding to a maximum damage of 50 displacements per atom (dpa). In Fe-5at%Cr alloy the Cr solute concentration remains unaltered even after a damage of 50 dpa. In the 10at%Cr the Cr solute concentration is reduced, with the increase of damage, asymptotically to a value of 7.2 at%.
ABSTRACT
We present a combined experimental and computational study of high temperature magnetic properties of Fe-Cr alloys with chromium content up to about 20 at.%. The magnetic cluster expansion method is applied to model the magnetic properties of random Fe-Cr alloys, and in particular the Curie transition temperature, as a function of alloy composition. We find that at low (3-6 at.%) Cr content the Curie temperature increases with the increase of Cr concentration. It is maximum at approximately 6 at.% Cr and then decreases for higher Cr content. The same feature is found in thermo-magnetic measurements performed on model Fe-Cr alloys, where a 5 at.% Cr alloy has a higher Curie temperature than pure Fe. The Curie temperatures of 10 and 15 at.% Cr alloys are found to be lower than the Curie temperature of pure Fe.