ABSTRACT
The intrinsic Fe local magnetic moment and Fe orbital occupations of iron-based superconductors are unveiled through the local, real-space capability of aberration-corrected scanning transmission electron microscopy/electron energy loss spectroscopy (STEM/EELS). Although the ordering of Fe moments needs to be suppressed for superconductivity to arise, the local, fluctuating Fe magnetic moment is enhanced near optimal superconductivity.
ABSTRACT
We use multiscale techniques to determine the extent of local inhomogeneity and superconductivity in Ca0.86Pr0.14Fe2As2 single crystal. The inhomogeneity is manifested as a spatial variation of the praseodymium concentration, local density of states, and superconducting order parameter. We show that the high-Tc superconductivity emerges from cloverlike defects associated with Pr dopants. The highest Tc is observed in both the tetragonal and collapsed tetragonal phases, and its filamentary nature is a consequence of nonuniform Pr distribution that develops localized, isolated superconducting regions within the crystals.
ABSTRACT
High-pressure electrical resistance measurements have been performed on single crystal Ba(0.5)Sr(0.5)Fe(2)As(2) platelets to pressures of 16 GPa and temperatures down to 10 K using designer diamond anvils under quasi-hydrostatic conditions with an insulating steatite pressure medium. The resistance measurements show evidence of pressure-induced superconductivity with an onset transition temperature at â¼31 K and zero resistance at â¼22 K for a pressure of 3.3 GPa. The transition temperature decreases gradually with increasing pressure before completely disappearing for pressures above 12 GPa. The present results provide experimental evidence that a solid solution of two 122-type materials, i.e., Ba(1-x)Sr(x)Fe(2)As(2) (0 < x < 1), can also exhibit superconductivity under high pressure.