ABSTRACT
The effect of iron and yttrium additions on glass forming ability and corrosion resistance of Al88Y8-xFe4+x (x = 0, 1, 2 at.%) alloys in the form of ingots and melt-spun ribbons was investigated. The crystalline multiphase structure of ingots and amorphous-crystalline structure of ribbons were examined by a number of analytical techniques including X-ray diffraction, Mössbauer spectroscopy, and transmission electron microscopy. It was confirmed that the higher Fe additions contributed to formation of amorphous structures. The impact of chemical composition and structure of alloys on their corrosion resistance was characterized by electrochemical tests in 3.5% NaCl solution at 25 °C. The identification of the mechanism of chemical reactions taking place during polarization test along with the morphology and internal structure of the surface oxide films generated was performed. It was revealed that the best corrosion resistance was achieved for the Al88Y7Fe5 alloy in the form of ribbon, which exhibited the lowest corrosion current density (jcorr = 0.09 µA/cm2) and the highest polarization resistance (Rp = 96.7 kΩâcm2).
ABSTRACT
The aim of this work was to characterize the structure and corrosion properties of the MgCa4.5(Gd0.5) alloys surface treated by the micro-arc oxidation (MAO) process. The MgCa4.5 and MgCa4.5Gd0.5 alloy samples were processed by MAO in an electrolyte composed of NaOH (10 g/dm3), NaF (10 g/dm3), NaH2PO4 (5 g/dm3), Na2SiO2·5H2O (10 g/dm3) and water. Two different voltages (120 V and 140 V) were used in the MAO process. The alloys protected by an oxide layer formed in the MAO were then the subject of corrosion resistance tests in an environment simulating the human body (Ringer's solution). After the experiments, the resulting samples were investigated using SEM, XPS and EDS techniques. The addition of Gd affected the fragmentation of the coating structure, thereby increasing the specific surface; higher voltages during the MAO process increased the number and size of surface pores. Corrosion tests showed that the MgCa4.5Gd0.5 alloys were characterized by low polarization resistances and high corrosion current densities. The studies indicated the disadvantageous influence of gadolinium on the corrosion resistance of MgCa4.5 alloys. The immersion tests confirmed lower corrosion resistance of MgCa4.5Gd0.5 alloys compared to the referenced MgCa4.5 ones. The MgCa4.5 alloy with the MAO coating established at voltage 140 V demonstrated the best anticorrosion properties.
ABSTRACT
The aim of the work was to characterize the structure of Al65Cu20Fe15 alloy obtained with the use of conventional casting and rapid solidification-melt-spinning technology. Based on the literature data, the possibility of an icosahedral quasicrystalline phase forming in the Al-Cu-Fe was verified. Structure analysis was performed based on the results of X-ray diffraction, neutron diffraction, 57Fe Mössbauer and transmission electron microscopy. Studies using differential scanning calorimetry were carried out to describe the crystallization mechanism. Additionally, electrochemical tests were performed in order to characterize the influence of the structure and cooling rate on the corrosion resistance. On the basis of the structural studies, the formation of a metastable icosahedral phase and partial amorphous state of ribbon structure were demonstrated. The possibility of the formation of icosahedral quasicrystalline phase I-AlCuFe together with the crystalline phases was indicated by X-ray diffraction (XRD), neutron diffraction (ND) patterns, Mössbauer spectroscopy, high-resolution transmission electron microscopy (HRTEM) observations and differential scanning calorimetry (DSC) curves. The beneficial effect of the application of rapid solidification on the corrosive properties was also confirmed.