Acidic Gases Separation from Gas Mixtures on the Supported Ionic Liquid Membranes Providing the Facilitated and Solution-Diffusion Transport Mechanisms.

Nowadays, the imidazolium-based ionic liquids containing acetate counter-ions are attracting much attention as both highly selective absorbents of the acidic gases and CO2 carriers in the supported ionic liquid membranes. In this regard, the investigation of the gas transport properties of such membranes may be appropriate for better understanding of various factors affecting the separation performance and the selection of the optimal operating conditions. In this work, we have tested CH4, CO2 and H2S permeability across the supported ionic liquid membranes impregnated by 1-butyl-3-methylimidazolium acetate (bmim[OAc]) with the following determination of the ideal selectivity in order to compare the facilitated transport membrane performance with the supported ionic liquid membrane (SILM) that provides solution-diffusion mechanism, namely, containing 1-butyl-3-methylimidazolium tetrafluoroborate (bmim[BF4]). Both SILMs have showed modest individual gases permeability and ideal selectivity of CO2/CH4 and H2S/CH4 separation that achieves values up to 15 and 32, respectively. The effect of the feed gas mixture composition on the permeability of acidic gases and permeselectivity of the gas pair was investigated. It turned out that the permeation behavior for the bmim[OAc]-based SILM toward the binary CO2/CH4, H2S/CH4 and ternary CO2/H2S/CH4 mixtures was featured with high acidic gases selectivity due to the relatively low methane penetration through the liquid phase saturated by acidic gases.

Preparation and Characterization of Facilitated Transport Membranes Composed of Chitosan-Styrene and Chitosan-Acrylonitrile Copolymers Modified by Methylimidazolium Based Ionic Liquids for CO2 Separation from CH4 and N2.

CO2 separation was found to be facilitated by transport membranes based on novel chitosan (CS)-poly(styrene) (PS) and chitosan (CS)-poly(acrylonitrile) (PAN) copolymer matrices doped with methylimidazolium based ionic liquids: [bmim][BF4], [bmim][PF6], and [bmim][Tf2N] (IL). CS plays the role of biodegradable film former and selectivity promoter. Copolymers were prepared implementing the latest achievements in radical copolymerization with chosen monomers, which enabled the achievement of outstanding mechanical strength values for the CS-based membranes (75-104 MPa for CS-PAN and 69-75 MPa for CS-PS). Ionic liquid (IL) doping affected the surface and mechanical properties of the membranes as well as the gas separation properties. The highest CO2 permeability 400 Barrers belongs to CS-b-PS/[bmim][BF4]. The highest selectivity α (CO2/N2) = 15.5 was achieved for CS-b-PAN/[bmim][BF4]. The operational temperature of the membranes is under 220 °C.