ABSTRACT
In this paper, the superplastic behavior of the two-phase titanium alloy VT6 with an ultrafine-grained (UFG) structure produced by equal-channel angular pressing is examined. The deformation of specimens with a UFG structure was performed by upsetting in a temperature range of 650-750 °C and strain rate range of 1 × 10-4-5 × 10-1 s-1. Under these conditions, an increased strain-rate sensitivity coefficient m was observed. The calculation of apparent activation energy showed values in a range of 160-200 kJ/mol while the superplastic flow of the VT6 alloy was occurring. When superplastic behavior (SPB) was impeded, the energy Q grew considerably, indicating a change in mechanism from grain-boundary sliding (GBS) to bulk diffusion. A change in temperature and strain rate influenced the development of superplastic flow and the balance of relaxation processes. Microstructural analysis shows that the UFG state is preserved at upsetting temperatures of 650 and 700 °C. A decrease in strain rate and/or an increase in upsetting temperature promoted a more active development of recrystallization and grain growth, as well as α2-phase formation. In a certain temperature and strain-rate range of the UFG VT6 alloy, α2-phase plates were found, the formation of which was controlled by diffusion. The effect of the α2-phase on the alloy's mechanical behavior is discussed.
ABSTRACT
In this work, the strength properties and impact toughness of the ultrafine-grained (UFG) Ti-6Al-4V titanium alloy produced by severe plastic deformation (SPD) in combination with upsetting were studied, depending on the direction of crack propagation. In the billets processed by equal-channel angular pressing (ECAP), the presence of anisotropy of ultimate tensile strength (UTS) and ductility was observed, conditioned by the formation of a metallographic and crystallographic texture. At the same time, the ECAP-processed UFG alloy exhibited satisfactory values of impact toughness, ~0.42 MJ/m2. An additional upsetting of the ECAP-processed billet simulated the processes of shape forming/die forging and was accompanied by the development of recovery and recrystallization. This provided the "blurring" of texture and a reduction in the anisotropy of UTS and ductility, but a difference in impact toughness in several directions of fracture was still observed. It is shown that texture evolution during upsetting provided a significant increase in the crack propagation energy. The relationship between microstructure, texture and mechanical properties in different sections of the material under study is discussed.