ABSTRACT
Today, additive manufacturing (AM) is the most recent technology used to produce detailed and complexly built parts for a variety of applications. The most emphasis has been given to fused deposition modeling (FDM) in the development and manufacturing fields. Natural fibers have received attention in the area of 3D printing to be employed as bio-filters with thermoplastics, which have prompted an effort for more ecologically acceptable methods of manufacturing. The development of natural fiber composite filaments for FDM requires meticulous methods and in-depth knowledge of the properties of natural fibers and their matrices. Thus, this paper reviews natural fiber-based 3D printing filaments. It covers the fabrication method and characterization of thermoplastic materials blended with natural fiber-produced wire filament. The characterization of wire filament includes the mechanical properties, dimension stability, morphological study, and surface quality. There is also a discussion of the difficulties in developing a natural fiber composite filament. Last but not least, the prospects of natural fiber-based filaments for FDM 3D printing are also discussed. It is hoped that, after reading this article, readers will have enough knowledge regarding how natural fiber composite filament for FDM is created.
ABSTRACT
Fused Deposition Modeling (FDM) is capable of producing complicated geometries and a variety of thermoplastic or composite products. Thus, it is critical to carry out the relationship between the process parameters, the finished part's quality, and the part's mechanical performance. In this study, the optimum printing parameters of FDM using oil palm fiber reinforced thermoplastic composites were investigated. The layer thickness, orientation, infill density, and printing speed were selected as optimization parameters. The mechanical properties of printed specimens were examined using tensile and flexural tests. The experiments were designed using a Taguchi experimental design using a L9 orthogonal array with four factors, and three levels. Analysis of variance (ANOVA) was used to determine the significant parameter or factor that influences the responses, including tensile strength, Young's modulus, and flexural strength. The fractured surface of printed parts was investigate using scanning electron microscopy (SEM). The results show the tensile strength of the printed specimens ranged from 0.95 to 35.38 MPa, the Young's modulus from 0.11 to 1.88 GPa, and the flexural strength from 2.50 to 31.98 MPa. In addition, build orientation had the largest influence on tensile strength, Young's modulus, and flexural strength. The optimum printing parameter for FDM using oil palm fiber composite was 0.4 mm layer thickness, flat (0 degree) of orientation, 50% infill density, and 10 mm/s printing speed. The results of SEM images demonstrate that the number of voids seems to be much bigger when the layer thickness is increased, and the flat orientation has a considerable influence on the bead structure becoming tougher. In a nutshell, these findings will be a valuable 3D printing dataset for other researchers who utilize this material.