ABSTRACT
Although many bone substitutes have been designed and produced, the development of bone tissue engineering products that mimic the microstructural characteristics of native bone remains challenging. It has been shown that pore orientation within collagen scaffolds influences bone matrix formation by the endochondral route. In addition, that the unidirectional orientation of the scaffolds can limit the growth of blood vessels. However, a comparison between the amount of bone that can be formed in scaffolds with different pore orientations in addition to analyzing the effect of loading osteogenic and proangiogenic factors is still required. In this work we fabricated uni- and multidirectional collagen sponges and evaluated their microstructural, physicochemical, mechanical and biological characteristics. Although the porosity and average pore size of the uni- and multidirectional scaffolds was similar (94.5% vs. 97.1% and 260 µm vs. 269 µm, respectively) the unidirectional sponges had a higher tensile strength, Young's modulus and capacity to uptake liquids than the multidirectional ones (0.271 MPa vs. 0.478 MPa, 9.623 MPa vs. 3.426 MPa and 8000% mass gain vs. 4000%, respectively). Culturing of rat bone marrow mesenchymal stem cells demonstrated that these scaffolds support cell growth and osteoblastic differentiation in the presence of BMP-2 in vitro, although the pore orientation somehow affected cell attachment and differentiation. The evaluation of the ability of the scaffolds to support bone growth when loaded with BMP-2 or BMP-2 + VEGF in an ectopic rat model showed that they both supported bone formation. Histological analysis and quantification of mineralized matrix revealed that the pore orientation of the collagen scaffolds influenced the osteogenic process.
ABSTRACT
Collagen type I is the main organic constituent of the bone extracellular matrix and has been used for decades as scaffolding material in bone tissue engineering approaches when autografts are not feasible. Polymeric collagen can be easily isolated from various animal sources and can be processed in a great number of ways to manufacture biomaterials in the form of sponges, particles, or hydrogels, among others, for different applications. Despite its great biocompatibility and osteoconductivity, collagen type I also has some drawbacks, such as its high biodegradability, low mechanical strength, and lack of osteoinductive activity. Therefore, many attempts have been made to improve the collagen type I-based implants for bone tissue engineering. This review aims to summarize the current status of collagen type I as a biomaterial for bone tissue engineering, as well as to highlight some of the main efforts that have been made recently towards designing and producing collagen implants to improve bone regeneration.
ABSTRACT
In mammals, long bones are formed by ossification of a cartilaginous mould during early stages of development, through the formation of structures called the primary ossification centre, the secondary ossification centres (SOCs) and the physeal cartilages (PCs). The PC is responsible for long bone growth. The morphology of the PC and the SOCs varies during different stages of femoral growth. In this respect, several details involving the process of murine femoral development are lacking. In the present study, a morphological characterization of femur development from the embryonic period to adulthood in mice was studied using micro-computed tomography (micro-CT). To achieve this aim, femora were collected at embryonic day (E) 14.5, E16.5 and E18.5 and at postnatal day (P)1, P7, P14, P35, P46 and P52. CT images were obtained using a micro-CT scanner (X-SkyScan 1172; Micro Photonics) and analysed using the micro-CT 3D visualization software Mimics (Materialise NV, Leuven, Belgium) and NRecon (Micro Photonics). The results of the present study revealed that the femur and its PCs and SOCs undergo morphological changes during different stages of development, including changes in their shape as well as position and thickness. These changes may be due to the response of the femur to mechanical loads imposed by muscle surrounding the bone during these stages of development. The result of the present study is important to improve our knowledge related to ossification and growth patterns of mouse femur during development.