Leaching and mechanical behaviour of concrete manufactured with recycled aggregates.

The reuse of debris from building demolition is of increasing public interest because it decreases the volume of material to be disposed to landfill. This research is focused on the evaluation of the possibility of reusing recycled aggregate from construction or demolition waste (C&D) as a substitute for natural aggregate in concrete production. In most applications, cement based materials are used for building construction due to their cost effectiveness and performance; however their impact on the surrounding environment should be monitored. The interstitial pore fluid in contact with hydrated cementitious materials is characterized by persistent alkaline pH values buffered by the presence of hydrate calcium silicate, portlandite and alkaline ions. An experimental plan was carried out to investigate concrete structural properties in relation to alkali release in aqueous solution. Results indicate that the presence of recycled aggregate increases the leachability of unreactive ions (Na, K, Cl), while for calcium the substitution resulted in a lower net leaching. In spite of the lower mechanical resistance (40% less), such a waste concrete may be suggested as more environmentally sustainable.

Reuse of ground waste glass as aggregate for mortars.

This work was aimed at studying the possibility of reusing waste glass from crushed containers and building demolition as aggregate for preparing mortars and concrete. At present, this kind of reuse is still not common due to the risk of alkali-silica reaction between the alkalis of cement and silica of the waste glass. This expansive reaction can cause great problems of cracking and, consequently, it can be extremely deleterious for the durability of mortar and concrete. However, data reported in the literature show that if the waste glass is finely ground, under 75mum, this effect does not occur and mortar durability is guaranteed. Therefore, in this work the possible reactivity of waste glass with the cement paste in mortars was verified, by varying the particle size of the finely ground waste glass. No reaction has been detected with particle size up to 100mum thus indicating the feasibility of the waste glass reuse as fine aggregate in mortars and concrete. In addition, waste glass seems to positively contribute to the mortar micro-structural properties resulting in an evident improvement of its mechanical performance.

Use of rubble from building demolition in mortars.

Because of increasing waste production and public concerns about the environment, it is desirable to recycle materials from building demolition. If suitably selected, ground, cleaned and sieved in appropriate industrial crushing plants, these materials can be profitably used in concrete. Nevertheless, the presence of masonry instead of concrete rubble is particularly detrimental to the mechanical performance and durability of recycled-aggregate concrete and the same negative effect is detectable when natural sand is replaced by fine recycled aggregate fraction. An alternative use of both masonry rubble and fine recycled material fraction could be in mortars. These could contain either recycled instead of natural sand or powder obtained by bricks crushing as partial cement substitution. In particular, attention is focused on the modification that takes place when either polypropylene or stainless steel fibers are added to these mortars. Polypropylene fibers are added in order to reduce shrinkage of mortars, stainless steel fibers for improving their flexural strength. The combined use of polypropylene fibers and fine recycled material from building demolition could allow the preparation of mortars showing good performance, in particular when coupled with bricks. Furthermore, the combined use of stainless steel fibers and mortars containing brick powder seems to be an effective way to guarantee a high flexural strength.