Grafted Polymethylhydrosiloxane on Hierarchically Porous Silica Monoliths: A New Path to Monolith-Supported Palladium Nanoparticles for Continuous Flow Catalysis Applications.

Polymethylhydrosiloxane has been grafted on the surface of a hierarchically porous silica monolith using a facile catalytic reaction between Si-H and silanol to anchor the polymer. This easy methodology leads to the functionalization of the surface of a silica monolith, where a large amount of free Si-H bonds remain available for reducing metal ions in solution. Palladium nanoparticles of 15 nm have been synthesized homogeneously inside the mesopores of the monolith without any stabilizers, using a flow of a solution containing Pd2+. This monolith was used as column-type fixed bed catalyst for continuous flow hydrogenation of styrene and selective hydrogenation of 3-hexyn-1-ol, in each case without a significant decrease of the catalytic activity after several hours or days. Conversion, selectivity, and stereoselectivity of the alkyne hydrogenation can be tuned by flow rates of hydrogen and the substrate solution, leading to high productivity (1.57 mol g(Pd)-1 h-1) of the corresponding cis-alkene.

High-performance liquid chromatography separation of unsaturated organic compounds by a monolithic silica column embedded with silver nanoparticles.

The optimization of a porous structure to ensure good separation performances is always a significant issue in high-performance liquid chromatography column design. Recently we reported the homogeneous embedment of Ag nanoparticles in periodic mesoporous silica monolith and the application of such Ag nanoparticles embedded silica monolith for the high-performance liquid chromatography separation of polyaromatic hydrocarbons. However, the separation performance remains to be improved and the retention mechanism as compared with the Ag ion high-performance liquid chromatography technique still needs to be clarified. In this research, Ag nanoparticles were introduced into a macro/mesoporous silica monolith with optimized pore parameters for high-performance liquid chromatography separations. Baseline separation of benzene, naphthalene, anthracene, and pyrene was achieved with the theoretical plate number for analyte naphthalene as 36,000 m(-1). Its separation function was further extended to cis/trans isomers of aromatic compounds where cis/trans stilbenes were chosen as a benchmark. Good separation of cis/trans-stilbene with separation factor as 7 and theoretical plate number as 76,000 m(-1) for cis-stilbene was obtained. The trans isomer, however, is retained more strongly, which contradicts the long- established retention rule of Ag ion chromatography. Such behavior of Ag nanoparticles embedded in a silica column can be attributed to the differences in the molecular geometric configuration of cis/trans stilbenes.

Efficiency of short, small-diameter columns for reversed-phase liquid chromatography under practical operating conditions.

Prototype small-size (1.0mm I.D., 5cm long) columns for reversed-phase HPLC were evaluated in relation to instrument requirements. The performance of three types of columns, monolithic silica and particulate silica (2µm, totally porous and 2.6µm, core-shell particles) was studied in the presence of considerable or minimal extra-column effects, while the detector contribution to band broadening was minimized by employing a small size UV-detector cell (6- or 90nL). A micro-LC instrument having small system volume (<1µL) provided extra-column band variance of only 0.01-0.02µL(2). The three columns generated about 8500 theoretical plates for solutes with retention factor, k>1-3 (depending on the column), in acetonitrile/water mobile phase (65/35=vol/vol) at 0.05mL/min, with the instrument specified above. The column efficiency was lower by up to 30% than that observed with a 2.1mm I.D. commercial column. The small-size columns also provided 8000-8500 theoretical plates for well retained solutes with a commercial ultrahigh-pressure liquid chromatography (UHPLC) instrument when extra-column contributions were minimized. While a significant extra-column effect was observed for early eluting solutes (k<2-4, depending on column) with methanol/water (20/80=vol/vol) as weak-wash solvent, the use of methanol/water=50/50 as wash solvent affected the column efficiency for most analytes. The results suggest that the band compression effect by the weak-wash solvent associated with partial-loop injection may provide a practical means to reducing the extra-column effect for small-size columns, while the use of an instrument with minimum extra-column effect is highly desirable.

Synthesis of silver nanoparticles confined in hierarchically porous monolithic silica: a new function in aromatic hydrocarbon separations.

Silver nanoparticles (Ag NPs) have been homogeneously introduced into hierarchically porous monolithic silica columns with well-defined macropores and SBA-15-type hexagonally ordered mesopores by using ethanol as the mild reductant. Within the cylindrical silica mesopores treated with aminopropyl groups as the host, monocrystalline Ag NPs and nanorods are obtained after being treated in silver nitrate/ethanol solution at room temperature for different durations of reducing time. The loading of Ag NPs in the monolith can be increased to 33 wt % by the repetitive treatment, which also led to the formation of polycrystalline Ag nanorods in the mesopores. Although the bare silica column cannot separate aromatic hydrocarbons, good separation of those molecules by noncharged Ag NPs confined in the porous structure of the monolith has been for the first time demonstrated with the Ag NP-embedded silica column. The NP-embedded monolithic silica would be a powerful separation tool for hydrocarbons with different number, position, and configuration of unsaturated bonds.

New hierarchically porous titania monoliths for chromatographic separation media.

Separation media based on hierarchically porous titania (TiO(2)) monoliths for high-performance liquid chromatography (HPLC) have been successfully fabricated by the sol-gel process of titanium alkoxide in a mild condition utilizing a chelating agent and mineral salt. The as-gelled TiO(2) monoliths were subjected to a simple solvent exchange process from ethanol (EtOH) to H(2)O followed by drying and calcination. The resultant monolithic TiO(2) columns consist of anatase crystallites with the typical specific surface area of more than 200 m(2)/g. The resultant monolithic TiO(2) column calcined at 200 and 400°C exhibited a good separation performance for organophosphates as well as for polar benzene derivatives in the normal-phase mode.

Monolithic silica rod columns for high-efficiency reversed-phase liquid chromatography.

Chromatographic properties of a new type of monolithic silica rod columns were examined. Silica rod columns employed for the study were prepared from tetramethoxysilane, modified with octadecylsilyl moieties, and encased in a stainless-steel protective column with two polymer layers between the silica and the stainless-steel tubing. A 25 cm column provided up to 45,000 theoretical plates for aromatic hydrocarbons, or a minimum plate height of about 5.5 µm, at optimum linear velocity of ca. 2.3 mm/s and back pressure of 7.5 MPa in an acetonitrile-water (80/20, v/v) mobile phase at 40°C. The permeability of the column was similar to that of a column packed with 5 µm particles, with K(F) about 2.4×10(-14) m(2) (based on the superficial linear velocity of the mobile phase), while the plate height value equivalent to that of a column packed with 2.5 µm particles. Generation of 80,000-120,000 theoretical plates was feasible with back pressure below 30 MPa by employing two or three 25 cm columns connected in series. The use of the long columns enabled facile generation of large numbers of theoretical plates in comparison with conventional monolithic silica columns or particulate columns. Kinetic plot analysis indicates that the monolithic columns operated at 30 MPa can provide faster separations than a column packed with totally porous 3-µm particles operated at 40 MPa in a range where the number of theoretical plates (N) is greater than 50,000.

Sol-gel synthesis of macro-mesoporous titania monoliths and their applications to chromatographic separation media for organophosphate compounds.

We have developed a method of independently tailoring the macro- and mesoporous structures in titania (TiO2) monoliths in order to achieve liquid chromatographic separations of phosphorous-containing compounds. Anatase TiO2 monolithic gels with well-defined bicontinuous macropores and microstructured skeletons are obtained via the sol-gel process in strongly acidic conditions using poly(ethylene oxide) as a phase separator and N-methylformamide as a proton scavenger. Aging treatment of the wet gels in the mother liquor at temperatures of 100-200 degrees C and subsequent heat treatment at 400 degrees C allow the formation and control of mesoporous structures with uniform pore size distributions in the gel skeletons, without disturbing the preformed macroporous morphology. The monolithic TiO2 rod columns with bimodal macro-mesoporous structures possess the phospho-sensitivity and exhibit excellent chromatographic separations of phosphorus-containing compounds.

Semi-micro-monolithic columns using macroporous silica rods with improved performance.

Monolithic silica columns in semi-micro-format have been synthesized using poly(acrylic acid) as a phase-separation inducer via a sol-gel route. The absence of a thick skin layer accompanied by deformation of the micrometer-sized gelling skeletons on the outermost part of the macroporous silica rod contributed to improve the efficiency of monolithic silica columns as thick as 2.4 mm in diameter. The kinetic plot analysis revealed that monolithic silica columns with macropore diameter of 1 microm and skeleton thickness of 1 microm with decreased macroporosity behave similarly to columns packed with 3 microm particles with slightly lower back pressure.

High-throughput protein digestion by trypsin-immobilized monolithic silica with pipette-tip formula.

Based on the monolithic silica gel materials with hierarchical pore structure and on the SPE devices (MonoTip) developed thereof, a trypsin-immobilized monolithic silica in a pipette tip (MonoTip Trypsin) suitable for digesting proteins has been newly developed. The surface of monolithic silica fixed into the tip was chemically modified with trypsin via an aminopropyl group. Trypsin-immobilized monolith successfully performed a rapid digestion of reduced and alkylated proteins with only a few times pipetting operation for the pre-treatment procedure of chromatographic analysis. The novel solid-phase digestion tool using monolithic silica allows a high-throughput trypsin proteolysis of bio-substances in proteomics.

Titania-coated monolithic silica as separation medium for high performance liquid chromatography of phosphorus-containing compounds.

A method of preparing titania-coated monolithic silica stationary phase has been developed to achieve liquid chromatographic separation of phosphorus-containing compounds, which have recently been attracting increasing attention in biochemical research. The titania-coated silica columns exhibited efficient separation with low pressure drop, which is a typical feature of monolithic structures, and also possessed phospho-selectivity, which is a unique property of the titania surface. The material characteristics of titania-coated monolithic silica were examined, and then resin-clad columns were applied to the HPLC analysis of phosphorylated compounds. Highly efficient separation of phosphorylated substances indicated that the novel titania-coated monolithic silica column will find applications as a useful tool in the field of biochemistry, especially in post-genomic analyses.

Development of a monolithic silica extraction tip for the analysis of proteins.

In proteomics, pre-treatment of sample is the most important procedure to remove the matrix for interfacing with mass spectrometry (MS). Additionally, for the samples with low concentration, the process of pre-concentration is required before MS analysis. We have newly developed solid-phase extraction (SPE) tool with pipette-tip shape for purification of bio-samples of various characteristics, utilizing monolithic silica gel as medium. The monolithic silica surface was modified with a C18 phase or coated with titania phase. A C18-bonded tip and a non-modified tip were used for sample concentration, desaltination and removal of detergents from sample. A titania-coated tip was also applied for purification and concentration of phosphorylated peptides. This novel pre-treatment method using monolithic silica extraction tip is much effective and suitable for protein analysis.

Microanalysis for MDR1 ATPase by high-performance liquid chromatography with a titanium dioxide column.

MDR1 is clinically important because it is involved in multidrug resistance of cancer cells and affects the pharmacokinetics of various drugs. Because MDR1 harnesses adenosine 5'-triphosphate (ATP) hydrolysis for transporting drugs, examining the effect on ATPase activity is imperative for understanding the interactions between drugs and MDR1. However, conventional assay systems for ATPase activity are not sensitive enough for screening drugs using purified MDR1. Here we report a novel method to measure ATPase activity of MDR1 using high-performance liquid chromatography equipped with a titanium dioxide column. The amount of adenosine 5'-diphosphate (ADP) produced by the ATPase reaction was determined within 2 min with a titanium dioxide column (4.6 mm ID x 100 mm). The relationship between ADP amount and chromatogram peak area was linear from 5 pmol to 10 nmol. This method made it possible to reduce the amount of purified MDR1 required for a reaction to 0.5 ng, about 1/20th of the conventional colorimetric inorganic phosphate detection assay. This method is sensitive enough to detect any subtle changes in ATPase activity of MDR1 induced by drugs and can be applied to measure ATPase activity of any protein.