ABSTRACT
Wastewater, which is rich with heavy elements, dyes, and pesticides, represents one of the most important environmental pollutants. Thus, it has been significant to fabricate environmentally friendly polymers with high adsorption ability for those pollutants. Herein, crosslinked chitosan (C-Cs) was prepared using isopropyl acrylamide and methylene bisacrylamide. Carbon nanoparticles (C-NPs) were also obtained by the treatment of the agricultural wastes, which was used with C-Cs to prepare C-Cs/C-NPs nanocomposite (C-Cs/C-NC). Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and transmission electron microscope (TEM) were used to investigate the prepared adsorbent. C-Cs, C-NPs, and C-Cs/C-NC were used in water treatment for the adsorption of lead ions (Pb+2) and methylene blue (MB). The adsorption process occurred by the prepared samples was investigated under different conditions, including contact time, as well as different doses and concentrations of adsorbents. The findings exhibited that the adsorption of Pb+2 and MB by C-Cs/C-NC was higher than C-Cs and C-NPs. In addition, the kinetic and isotherm models were studied, where the results showed that the adsorption of Pb+2 and MB by various adsorbents obeys pseudo-second-order and Langmuir isotherms, respectively.
ABSTRACT
Rice husk (RH), an abundant agricultural residue, was reacted with 2-bromoisobutyryl bromide, to convert it to a heterogeneous polyfunctional macroinitiator for Atom Transfer Radical Polymerization (ATRP). The number of active sites placed on the RH surface was small, but they were ATRP active. Non-polar methyl methacrylate (MMA) and polar acrylonitrile (AN) were polymerized from the RH, and a sequential monomer addition was used to prepare an amphiphilic PMMA-b-PAN copolymer on RH surface. FTIR qualitatively confirmed the grafting. Gravimetric and XPS analysis of the different RH surface compositions indicated thin layers of oligomeric PMMA, PAN, and PMMA-b-PAN. The modified surfaces were mapped by nanomechanical AFM to measure surface roughness, and adhesion and moduli using the Derjaguin-Muller-Toropov model. RH grafted with MMA possessed a roughness value of 7.92, and a hard and weakly adhering surface (13.1 GPa and 16.7 nN respectively) while RH grafted with AN yielded a roughness value of 29 with hardness and adhesion values of 4.0 GPa and 23.5 nN. The PMMA-b-PAN modification afforded a surface with a roughness value of 51.5 nm, with hardness and adhesion values of 3.0 GPa and 75.3 nN.