ABSTRACT
The fear of a missing tooth often leads to postponing the visit at the dentist. While extraction itself is a major stressful experience for the patient, the presence of visible gaps or missing teeth inside or outside the aesthetic zone is a deal breaker for a lot of patients. Bridging the time spent until inserting any final restoration with a provisional enables the patients to still take part in everyday life. This case report shows a new approach for a fixed dental provisional in the anterior region using a printed wing bridge approach to replace an extracted tooth. The provisional was prefabricated, and extraction and integration of the provisional could be placed in a single visit. The chosen approach shows the integrability of 3D printing in everyday practice providing immediate economical and aesthetic treatment.
ABSTRACT
This study aimed to analyze the influence of multiple uses of zirconia implant drills on their cutting performance and bending strength. The hypothesis was that drill usage and sterilization cycles would not affect drilling time or flexural strength. Sixty zirconia twist drills from Z-Systems were used to drill in the angulus mandibulae region of fresh porcine jaws. The drills were divided into four groups based on the cycle count, and the drilling time was measured. Bending strength tests were conducted using a universal testing machine, and statistical analysis was performed using ANOVA tests. The results showed that drilling times followed a normal distribution, and significant differences were observed in drilling times between group 1 and the other groups for the pilot drill. However, no significant differences were found for ø3.75 mm and ø4.25 mm drills, and drilling times also varied significantly among different drill diameters, regardless of the cycle count. Flexural strength did not significantly differ among drill diameters or sterilization cycles. Overall, using and sterilizing zirconia implant drills had no significant impact on drilling time or flexural strength. Nevertheless, drilling times did vary depending on the diameter of the drill. These findings provide valuable insights into the performance and durability of zirconia implant drills, contributing to the optimization of dental implant procedures.
ABSTRACT
Background: Purpose of this study was to investigate the mechanical efficiency of 3D-printed permanent and provisional implant cemented fixed bridges produced via CAD/CAM technology using an interim and a permanent ceramic filled hybrid material. Material and Methods: Two groups with twenty specimens each were designed and 3D-printed via digital light processing technology (DLP). A fracture strength test was performed. Statistical analysis was performed (p>0.05) for impression distance and force. Results: For the fracture resistance and impression distance no significant difference (p = 0.643) were detected. The specimens of interim resin showed a mean value of 365.90 ± 86.67 N. Whereas specimens of permanent ceramic filled hybrid material showed a mean value of 363.45 ± 87.57 N. Conclusions: In this in vitro study 3D-printed ceramic filled hybrid material and interim resin based on methacrylic acid esters showed an acceptable resistance to bite forces with no differences in fracture mechanism. Key words:CAD-CAM, dental resin, 3D printing.
ABSTRACT
Particularly severe cases with tunneled defects are rarely reported and are described only in a few case reports. This case report describes the treatment of a tunnel fenestration in the lower central jaw after unsuccessful endodontic treatment following trauma of incisors 31 and 41 over the course of six years, which led to the development of an internal granuloma and a radicular cyst in the lower jaw. The patient presented with a 2.67 cm3 radicular cyst displacing the surrounding tissue at regio 31 and 41, which resulted in a tunnel-like bony defect. Endodontic treatment and periapical root tip resection on teeth 31 and 41 with cystectomy, and with a 12 month follow-up, were successful in the healing of the bone defect. The preserved teeth received lithium disilicate crowns for definite restoration one year postoperatively. This treatment can be an option for the therapy of large cysts.
ABSTRACT
PURPOSE: The aim of this study was to investigate to what extent cyclic load affects the screwless implant-abutment connection for Morse taper dental implants. MATERIALS AND METHODS: 16 implants (SICvantage max) and 16 abutments (Swiss Cross) were used. The screwless implant-abutment connection was subjected to 10,000 cycles of axial loading with a maximum force of 120 N. For the pull-off testing, before and after the same cyclic loading, the required force for disconnecting the remaining 6 implant-abutment connections was measured. The surface of 10 abutments was examined using a scanning electron microscope 120× before and after loading. RESULTS: The pull-off test showed a significant decrease in the vertical force required to pull the abutment from the implant with mean 229.39 N ± 18.23 before loading, and 204.30 N ± 13.51 after loading (P<.01). Apart from the appearance of polished surface areas and slight signs of wear, no visible damages were found on the abutments. CONCLUSION: The deformation on the polished abutment surface might represent the result of micro movements within the implant-abutment connection during loading. Although there was a decrease of the pull-off force values after cyclic loading, this might not have a notable effect on the clinical performance.