Enhanced adsorption for trivalent antimony by nano-zero-valent iron-loaded biochar: performance, mechanism, and sustainability.

The discharge of tailing leachate and metallurgical wastewater has led to an increasing trend of water pollution. In this study, nZVI-modified low-temperature biochar was used to adsorb Sb(III) from water. The adsorption capacity and speed of nZVI-BC were better than those of BC, and the best adsorption effect was observed for 4nZVI-BC, with 93.60 mg·g-1 maximum adsorptive capacity, which was 208.61% higher than the original BC. The Langmuir and Temkin models were well fitted (R2 ≥ 0.99), and PSO was more in line with the 4nZVI-BC adsorption process, indicating that the adsorption was a monolayer physico-chemical adsorption. The combination of XRD, FTIR, and XPS characterization demonstrated that the adsorption mechanism predominantly included redox reactions, complexation, and electrostatic interactions. The thermodynamic results demonstrated that 4nZVI-BC adsorption on Sb(III) was a spontaneous endothermic process. Additionally, the order of the influence of interfering ions on 4nZVI-BC was CO32- > H2PO4- > SO42- > Cl-. After three repeated uses and adsorption-desorption, the adsorption ratio of Sb(III) by 4nZVI-BC was still as high as 90% and 65%, respectively. This study provides a theoretical reference for the exploration and development of Sb(III) removal technologies for aquatic environments.

Trivalent antimony removal using carbonaceous nanomaterial loaded with zero-valent bimetal (iron/copper) and their effect on seed growth.

As rapid industrial and social growth, antimony mines are the overexploited, leading to the accumulation of trivalent antimony in the aquatic environment near smelters, which harm human health. To eradicate trivalent antimony from water, an innovative nanomaterial in the form of sludge biochar loaded with zero-valent bimetal was synthesized using a liquid-phase reduction method. The adsorption performance of the nanomaterial for trivalent antimony was investigated based on a series of adsorption experiments using sludge biochar, nano zero-valent iron biochar, and nano zero-valent bimetal biochar. The results showed that the optimal adsorption performance of the three nanomaterials for trivalent antimony, considering the economic practicability, was highlighted at solution pH of 3 and 0.05 g of nanomaterial. Additionally, the maximum adsorption capacity of sludge biochar, nano zero-valent iron biochar, and nano zero-valent bimetal biochar is 3.89 mg g-1 at 35 °C, 32.01 mg g-1 at 25 °C, 50.96 mg g-1 at 25 °C, respectively. The adsorption process of sludge biochar is endothermic, resulting in an increase in the adsorption capacity with increasing temperature, whereas the exothermic reaction contributes to decrease in the adsorption capacity at increasing temperature for the other two carbon nanomaterials. The inhibitory effect of coexisting ions was in the order: Al3+ > NH4+ > Na+ > K+; CO32- > CH3COO- > H2PO4- > S2-. Additionally, nanomaterials promoted seed germination and growth. Investigation of the adsorption mechanism using X-ray photoelectron spectroscopy showed that trivalent antimony was oxidised to pentavalent antimony, and Fe(III) was reduced to Fe(II). The formed primary battery formed by copper ions and iron acclerated electron transfer and improved the adsorption rate. This implied that trivalent antimony could be removed through the synergistic action of the adsorption behaviour and redox reaction. Therefore, the biochar loaded with the zero-valent bimetal serves as a pathway for eradicating trivalent antimony.