Clinical Performance of Minimally Invasive Monolithic Ultratranslucent Zirconia Veneers: A Case Series up to Five Years of Follow-up.

There is a lack of reports in the literature on the long-term clinical performance of ultratranslucent zirconia, especially considering its use in manufacturing monolithic veneers. The purpose of this case series is to describe the aesthetic treatment steps of three patients with minimally invasive ultratranslucent zirconia veneers and to report the clinical findings up to five years. Three patients (woman: 2, man: 1; mean age: 30 years) unsatisfied with their dental aesthetics sought dental treatment. The treatment plan involved cementing ultratranslucent zirconia veneers. Air-abrasion was performed on the internal surface of zirconia with alumina particles coated by silica (silicatization), followed by silane and adhesive applications for the adhesive cementation. All veneers were adhesively cemented to enamel with resin cement (Variolink Esthetic, Ivoclar). The patients were clinically evaluated annually considering the Ryge modified/ California Dental Association criteria. After a mean follow-up of 4.33 years (4-5 years), a survival rate of 100% was detected for the 28 minimally invasive ultratranslucent zirconia veneers cemented in the 3 patients. There were no absolute failures such as debonding, veneer fracture, or secondary caries. Superficial marginal discoloration was observed in one element (maxillary left lateral incisor) of one patient. Ultratranslucent zirconia is a viable option for manufacturing veneers due to its excellent clinical performance and longevity. However, further long-term clinical studies are essential to consolidate this material as an option for esthetic restorations.

Surface Treatment and Cementation of Lithium Silicate Ceramics Containing ZrO2.

OBJECTIVE: To evaluate the effect of different surface treatments on the shear bond strength (SBS) of lithium silicate (LS) and lithium disilicate (LD) ceramics, after thermocycling. METHODS AND MATERIALS: For SBS test, 72 ceramic blocks (18×14×2 mm) were made (24 blocks from each ceramic material): VITA Suprinity (LSS), Celtra Duo (LSC), and Lithium disilicate (LD). The blocks were polished with sandpaper of increasing grit (#280, #400, #800, and #1200) and embedded in chemically activated acrylic resin. Afterwards, they were randomly divided into 12 groups (6 blocks per group) according to: "Ceramic" (LD, LSC, and LSS) and "Surface treatment" (HFS: hydrofluoric acid + silane; MEP: Monobond Etch & Prime/Ivoclar). From each treated surface ceramic block, four dual-curing resin cement cylinders (RelyX U200, 3M Oral Care) were prepared using a Tygon tube (Ø=3 mm and h=2 mm) and light cured for 40 seconds (1000 mW/cm2) (N=288/n=24). All specimens were submitted to thermocycling (10,000 cycles, 5°C and 55°C, 30 seconds) and then to SBS test at a crosshead speed of 1 mm/min using a 50-kgf load cell. Forty-five additional blocks were made for roughness and SEM analysis. Failure mode was also performed. The data (MPa) were statistically analyzed by oneway analysis of variance (ANOVA), Tukey test (5%), and Weibull analysis. The Ra was analyzed by Kruskal-Wallis and Dunn Test (5%). The other variables were analyzed qualitatively. RESULTS: ANOVA revealed that "surface treatment" was significant for all ceramic materials (p<0.05). The LD-HFS (18.66±3.49), LSC-HFS (16.81±2.62), and LSS-HFS (16.33±3.08) groups had significantly higher SBS than the LD-MEP (7.00±4.2), LSCMEP (14.12±3.51), and LSS-MEP (13.87±2.52) groups. Complete adhesive failures at the cement-dentin interface were more frequent. Weibull modulus was superior for the LD-HFS (6.22), LSC-HFS (8.8), and LSS-HFS (7.4) groups. CONCLUSION: HF followed by silanization is the most suitable surface treatment for the cementation of LS and LD glass ceramics.

Two-year Follow-up of Ceramic Veneers and a Full Crown Treated With Self-etching Ceramic Primer: A Case Report.

CLINICAL RELEVANCE: The Monobond Etch & Prime seems to be an efficient option for adhesive cementation of ultrathin veneers and full crown ceramic with good properties after two years of clinical follow-up. SUMMARY: The use of the self-etching ceramic primer combines the stages of acid conditioning and silanization in cementation procedures of ceramic restorations. The protocol is a simpler and safer alternative to the conventional protocol for surface treatment of silica-based ceramics. This case report describes the steps of an esthetic rehabilitation with ultrathin veneers and full crown based on lithium disilicate treated with a ceramic primer (Monobond Etch & Prime, Ivoclar Vivadent, Schaan, Liechtenstein). After two years of clinical follow-up, the restorations presented satisfactory esthetic and functional performance, color stability, surface and marginal integrity, and absence of cracks and debonding. More research is needed to investigate the clinical performance and longevity of the ceramic restorations treated with self-etching ceramic primers.