ABSTRACT
This investigation introduces the first estimation of ternary reactivity ratios for a butyl acrylate (BA), 2-methylene-1,3-dioxepane (MDO), and vinyl acetate (VAc) system at 50 °C, with an aim to develop biodegradable pressure-sensitive adhesives (PSAs). In this study, we applied the error-in-variables model (EVM) to estimate reactivity ratios. The ternary reactivity ratios were found to be r12 = 0.417, r21 = 0.071, r13 = 4.459, r31 = 0.198, r23 = 0.260, and r32 = 55.339 (BA/MDO/VAc 1/2/3), contrasting with their binary counterparts, which are significantly different, indicating the critical need for ternary system analysis to accurately model multicomponent polymerization systems. Through the application of a recast Alfrey-Goldfinger model, this investigation predicts the terpolymer's instantaneous and cumulative compositions at various conversion levels, based on the ternary reactivity ratios. These predictions not only provide crucial insights into the incorporation of MDO across different initial feed compositions but also offer estimates of the final terpolymer compositions and distributions, underscoring their potential in designing compostable or degradable polymers.
ABSTRACT
Different cellulose nanocrystal (CNC) forms (dried vs never-dried) can lead to different degrees of CNC reassembly, the formation of nanofibril-like structures, in nanocomposite latex-based pressure-sensitive adhesive (PSA) formulations. CNC reassembly is also affected by CNC sonication and loading as well as the protocol used for CNC addition to the polymerization. In this study, carboxylated CNCs (cCNCs) were incorporated into a seeded, semibatch, 2-ethylhexyl acrylate/methyl methacrylate/styrene emulsion polymerization and cast as pressure-sensitive adhesive (PSA) films. The addition of CNCs led to a simultaneous increase in tack strength, peel strength, and shear adhesion, avoiding the typical trade-off between the adhesive and cohesive strength. Increased CNC reassembly resulted from the use of dried, redispersed, and sonicated cCNCs, along with increased cCNC loading and addition of the cCNCs at the seed stage of the polymerization. The increased degree of CNC reassembly was shown to significantly increase the shear adhesion by enhancing the elastic modulus of the PSA films.