3D-printed polyether-ether ketone/carboxymethyl cellulose scaffolds coated with Zn-Mn doped mesoporous bioactive glass nanoparticles.

Patient-specific fabrication of scaffold/implant requires an engineering approach to manufacture the ideal scaffold. Herein, we design and 3D print scaffolds comprised of polyether-ether-ketone (PEEK) and sodium-carboxymethyl cellulose (Na-CMC). The fabricated scaffold was dip coated with Zn and Mn doped bioactive glass nanoparticles (Zn-Mn MBGNs). The synthesized ink exhibit suitable shear-thinning behavior for direct ink write (DIW) 3D printing. The scaffolds were crafted with precision, featuring 85% porosity, 0.3 mm layer height, and 1.5 mm/s printing speed at room temperature. Scanning electron microscopy images reveal a well-defined scaffold with an average pore size of 600 ± 30 µm. The energy dispersive X-ray spectroscopy analysis confirmed a well dispersed/uniform coating of Zn-Mn MBGNs on the PEEK/Na-CMC scaffold. Fourier transform infrared spectroscopy approved the presence of PEEK, CMC, and Zn-Mn MBGNs. The tensile test revealed a Young's modulus of 2.05 GPa. Antibacterial assays demonstrate inhibition zone against Staphylococcus aureus and Escherichia Coli strains. Chick Chorioallantoic Membrane assays also present significant angiogenesis potential, owing to the antigenic nature of Zn-Mn MBGNs. WST-8 cell viability assays depicted cell proliferation, with a 103% viability after 7 days of culture. This study suggests that the PEEK/Na-CMC scaffolds coated with Zn-Mn MBGNs are an excellent candidate for osteoporotic fracture treatment. Thus, the fabricated scaffold can offer multifaceted properties for enhanced patient outcomes in the bone tissue regeneration.

3D Printing Assisted Fabrication of Copper-Silver Mesoporous Bioactive Glass Nanoparticles Reinforced Sodium Alginate/Poly(vinyl alcohol) Based Composite Scaffolds: Designed for Skin Tissue Engineering.

Additive manufacturing (also known as 3D printing) is a promising method for producing patient-specific implants. In the present study, sodium alginate (Na-ALG)/poly(vinyl alcohol) (PVA) polymer blends of varying ratios (1:0, 3:1, 1:1, and 1:3) were used to produce tailored-designed skin scaffolds using a 3D bioprinter. Samples of skin scaffolds were printed at 20 layers with a layer height of 0.15 mm using a needle with an inner diameter of 330 µm while maintaining the extrusion speed, extrusion width, and fill density at 10 mm/s, 0.2 mm, and 85%, respectively. The Na-ALG/PVA blend with a 3:1 ratio showed the best printability due to its good viscosity and minimal nozzle leakage, allowing for the fabrication of skin scaffolds with high fidelity and the desired morphological characteristics. Then, copper-silver doped mesoporous bioactive glass nanoparticles (Cu-Ag MBGNs) were incorporated into the Na-ALG/PVA blend (which had already been prepared by using a Na-ALG:PVA ratio of 3:1) in order to obtain therapeutic (angiogenic and antibacterial) effects. The fabricated Na-ALG/PVA/Cu-Ag MBGNs biocomposite scaffolds with dimensions of 20 mm× 20 × 3 mm3 and pore size of 400 ± 60 µm exhibited a promising fidelity. The presence of chemical bonds attributed to Na-ALG, PVA, and Cu-Ag MBGNs and the uniform distribution of Na, C, and O elements within the microstructure of the scaffolds were confirmed by EDX, SEM, and FTIR analyses. The scaffolds were hydrophilic and exhibited proper swelling and degradation behavior for skin tissue engineering. According to the inhibition halo test, the scaffolds exhibited strong antibacterial activity against Staphylococcus aureus and Escherichia coli. The cytocompatibility to human-derived fibroblast cells was confirmed by the WST-8 assay and in vivo Chorioallantoic Membrane Assay. In addition, Na-ALG/PVA/Cu-Ag MBGNs showed angiogenic potential, exhibiting favorable wound healing properties.