ABSTRACT
Objective To analyze bond strength to bleached enamel following application of 10% sodium ascorbate gel. Material and methods Forty third molars were allocated into five groups (n = 8): GP - unbleached specimens restored with composite resin; GN - specimens restored immediately after bleaching; and G15; G30 and G60 (test groups) - bleached specimens treated with 10% sodium ascorbate gel for 15, 30 and 60 min before restoration. The teeth were sectioned and the buccal and lingual faces were restored. After storage in distilled water (37 °C/24 h), sticks of ±0.8 mm2 were tested in tensile (0.5 mm/min). Fractures were observed and classified. Data (in MPa) were analyzed with one-way ANOVA and Tukey tests (α = 0.05). Results No differences were found among GP (26 ± 6.0), G15 (23 ± 7.3), G30 (25 ± 6.1) and G60 (25 ± 5.1), with GN (15 ± 5.5) showing the lowest bond strength (p < 0.0001). Conclusion The application of 10% sodium ascorbate gel for 15 min after bleaching with 37.5% hydrogen peroxide restored the bonding to enamel.
ABSTRACT
OBJECTIVE: This study evaluated the effect of air temperature (warm or cold) for solvent evaporation on bonding and nanoleakage of self-etching adhesives to dentin. MATERIALS AND METHODS: The adhesives Clearfil 3S Bond [S3], OptiBond All-In-One [OB], Adper SE Plus [AD], and Silorane adhesive [SI] were applied on dentin surfaces, and a warm (60 ± 2°C) or cold air (20 ± 1°C) was applied and light-cured. After water storage (24 h), the teeth were sectioned into sticks (0.8 mm(2)) and tested in tensile. Then, they were immersed in a 50% solution of silver nitrate, photo-developed and the nanoleakage observed in a scanning electron microscope. The bond strength and nanoleakage pattern were analyzed by two-way analysis of variance and post hoc Tukey's test (α =0.05). RESULTS: Higher bond strength and lower silver nitrate uptake were observed for the adhesives under warm condition (P < 0.05). AD and SI showed better adhesive results than S3 and OB (P < 0.05). CONCLUSION: The use of a warm air was useful to improve the bonding and diminish the nanoleakage of adhesive systems to dentin.
ABSTRACT
Este trabalho foi desenvolvido com o objetivo de avaliar in vitro a resistência adesiva em reparos de resina composta em corpos de prova submetidos a testes de tração. Após permanecerem armazenados em água destilada durante quinze dias, 80 meio-espécimes de resina composta microhíbrida Esthet-X (Dentsply) tiveram a interface do reparo desgastada com uma ponta diamantada, condicionada por trinta segundos com ácido fosfórico 37%, lavada, e seca. Os hemi-halteres foram divididos em quatro grupos de vinte espécimes, e cada grupo recebeu um sistema adesivo: Grupo I: uma camada de adesivo Prime&Bond 2.1 (Dentsply); Grupo II: uma camada de silano (Silano - Dentsply) seguida de uma camada de adesivo; Grupo III: uma camada de silano; Grupo IV: três camadas de silano. Os espécimes foram completados com a inserção da mesma resina composta, mantidos em água destilada novamente, por 24 horas, e submetidos a teste de tração na máquina de ensaio universal EMIC. Os testes estatísticos aplicados foram Análise de Variância a um critério - ANOVA - seguido de Teste de Tukey (p<5%). Os resultados obtidos foram (média ± desvio padrão) para o Grupo I: 28,93 ± 7,68; Grupo II: 27,87 ± 9,57; Grupo III: 20,59 ± 5,82 e Grupo IV: 22,0 ± 6,69, demonstrando que a aplicação de adesivo tem influência positiva, estatisticamente significante na resistência à tração, comparando com a aplicação isolada do silano. A associação adesivo/silano não demonstrou vantagem em relação ao uso isolado do agente adesivo, e o uso de três camadas de silano não elevou a resistência adesiva comparada com a aplicação da camada única