ABSTRACT
In this work, we report a large-area fabrication of a flexible superhydrophobic bactericidal surface decorated with copper hydroxide nanowires. This involves a simple two-step method which involves growth followed by transfer of the nanowires onto the polydimethylsiloxane (PDMS) surface by mechanical peeling. Additional roughness in PDMS is obtained through incomplete wetting of the nanoscale gaps which leads to dual-scale roughness and superhydrophobicity with a contact angle of 169° and hysteresis of less than 2°. The simplicity of the process makes it low-cost and easily scalable. The process allows fabrication of nonplanar 3D surfaces. The surface shows blood repellence and antibacterial activity against Escherichia coli with more than 5 log reductions in bacterial colony. The surface also shows hemocompatible behavior, making it suitable for healthcare applications. The fabricated surface is found to be extremely robust against stretching, twisting, sandpaper abrasion, solid weight impact, and tape peel test. The surface is found to withstand human weight multiple times without losing its hydrophobicity, making it suitable for several practical scenarios in healthcare and household applications.
ABSTRACT
We propose robust and scalable processes for the fabrication of floating gate devices using ordered arrays of 7 nm size gold nanoparticles as charge storage nodes. The proposed strategy can be readily adapted for fabricating next generation (sub-20 nm node) non-volatile memory devices.
Subject(s)
Computer Storage Devices , Crystallization/methods , Gold/chemistry , Nanostructures/chemistry , Nanostructures/ultrastructure , Nanotechnology/instrumentation , Equipment Design , Equipment Failure Analysis , Materials Testing , Particle SizeABSTRACT
We show that the substrate affects the interparticle spacing in monolayer arrays with hexagonal order formed by self-assembly of polymer grafted nanoparticles. Remarkably, arrays with square packing were formed due to convective shearing at a liquid surface induced by miscibility of colloidal solution with the substrate.