ABSTRACT
In this work, photocatalytic materials constituted by Cr-doped TiO2 (Cr-TiO2) decorated with noble metals show high effectiveness in the mineralization of Acid Orange 7 (AO7) and in the disinfection of real river water. The materials were firstly obtained by sol-gel method to get Cr-TiO2 that was subsequently modified by photochemical deposition of Ag or Pd nanoparticles (Ag/Cr-TiO2, Pd/Cr-TiO2). Chemical-physical characterization results evidenced that the noble metals were homogeneously distributed on the Cr-TiO2 surface. By using Pd(0.25%)/Cr-TiO2, the AO7 discoloration efficiency was about 91.4% after only 60 min of visible irradiation, which can be due to the lowest band gap of this material. Moreover, nitrates, chlorides, total hardness, and coliform bacteria content significantly decreased after the treatment of real river water samples (that is contaminated by industrial and domestic effluents) under UV and visible light irradiation in the presence of TiCrOx decorated with noble metals. One hundred percent of elimination rate for E. coli, total coliforms, and other enterobacteriaceae (without regrowth) was achieved by using Ag/Cr-TiO2 as photocatalyst.
ABSTRACT
In this study, titanium dioxide powder obtained by the sol-gel method and TiO2 nanotubes, were prepared. In order to increase the TiO2 photoactivity, the powders and nanotubes obtained were modified by dye sensitization treatment during the oxide synthesis. The sensitizers applied were Quinizarin (Q) and Zinc protoporphyrin (P). The materials synthesized were extensively characterized and it was found that the dye sensitization treatment leads to modify the optical and surface properties of Titania. It was also found that the effectiveness of the dye-sensitized catalysts in the phenol and methyl orange (MO) photodegradation strongly depends on the dye sensitizer employed. Thus, the highest degradation rate for MO was obtained over the conventional Q-TiO2 photocatalyst. In the case of the nanotubes series, the most effective photocatalyst in the MO degradation was based on TiO2-nanotubes sensitized with the dye protoporfirin (ZnP). Selected catalysts were also tested in the phenol and MO photodegradation under visible light and it was observed that these samples are also active under this radiation.