ABSTRACT
In the present work, pure nanocrystalline monoclinic Zirconia (ZrO2) has been successfully synthesized and optimized by the modified co-precipitation method. The concentration of raw material has been optimized with the fixed amount of precipitation agent (Potassium hydroxide KOH). The thermal history of the precursor has been examined through TG/DTA analysis. All the samples are subjected to study the structure, fingerprints of the molecular vibrations, and morphology analyses. The representative sample has been analyzed through Transmission Electron Microscope (TEM) and X-ray Photo Electron Spectroscopy (XPS) analyses. The as-prepared sample exhibits the better crystallinity and surface morphology with lesser particle size (190 nm) when the raw material concentration is 0.2 M. The as-prepared ZrO2 filler (0, 3, 6, 9, and 12 wt.%) is spread through the enhanced polymer electrolyte P(S-MMA) (27 Wt.%)-LiClO4 (8 wt.%)-EC + PC (1;1 of 65 wt.%) complex system via solution casting method. The as-synthesized electrolyte films are examined via complex impedance analysis. P(S-MMA) (27 wt.%)-LiCIO4 (8 wt.%)-EC + PC (1 ;1 of 65 wt.%)-6 wt.% of ZrO2 shows the high ionic conductivity 2.35 × 10-3 Scm-1. Temperature-dependent ionic conductivity studies obey the non-linear behavior. The enhanced ZrO2 has been expected to enhance the other electrochemical properties of the lithium secondary battery.
ABSTRACT
The present study emphases on the effect of toting of TiO2 filler on the electrochemical enactment of polymer electrolyte containing PVdF-co-HFP(30) + SEt3TFSI(10) + EC/PC(60) + TiO2(x) wt% (Poly (vinylidene fluoride-co-hexafluoropropylene + Triethylsulfoniumbis(trifluoromethylsulfonyl)imide + Ethylene carbonate/Propylene carbonate (1:1 ratio) + Titanium dioxide) for lithium battery applications. Composite electrolytes with different weight percentages of TiO2 were prepared and characterized by different surface analytical, thermal and electrochemical techniques. With gradual increase of the amount of TiO2 upto 6 wt%, broadening of the prominent peak has been noted, suggesting a decrease in the degree of crystallinity upon the addition of TiO2, as revealed by X-ray diffraction (XRD). Raman and FT-IR studies confirm the presence of various functional groups, present in the matrix. The electrolyte with TiO2 (6 wt%) has maximum stability of 460 °C, as confirmed by thermal analysis. Conductivity of the composite polymer electrolytes increases upto 6 wt% of TiO2 (3.42 × 10-3 S/cm at 303 K) and further addition, causes a dip down in conductivity, indicating an improvement in the ionic conductivity and thermal stability with the incorporation of TiO2 filler. Surface morphologic images show the presence of surface and cavity in the polymer matrix, filled with the filler uniformly. Voltammetric studies confirm the electrochemical stability of films upto 4.62 V. Coin cell containing Li anode and LiFePO4 cathode along with polymer electrolyte/6 wt% TiO2 filler, delivers a first discharge capacity of 145 mAh/g with the working voltage of 3.4 V.