ZnO-Enhanced Reduced Graphene Oxide Electrodes from Cocoa Shell: Nanoarchitectonics Platform for Photoelectrocatalytic Detection of Methylene Blue.

In this study, we report the successful preparation of reduced graphene oxide modified zinc oxide (rGO-ZnO) composites from cocoa shells. Synthesis of rGO-ZnO was carried out using the Hummer method and thermal reduction. The electrode material was comprehensively characterized using fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and scanning electron microscopy & Energy Dispersive X-ray (SEM-EDX). The photoelectrocatalytic performance of the prepared composite electrodes was evaluated using various electrochemical techniques, including Linear Sweep Voltammetry (LSV), Cyclic Voltammetry (CV), and Multi Pulse Amperometry (MPA). The FTIR analysis of rGO-ZnO exhibited distinct bands corresponding to C-O at 1022 cm-1, C=C at 1600 cm-1, and Zn-O at 455 cm-1. The XRD analysis revealed characteristic peaks at 26.6º, 29.2º, 36.2º, 44.04º, 47.58º, and 64.4º, confirming the presence of key crystalline phases. SEM-EDX analysis of rGO-ZnO revealed a rough surface morphology with bright white and black regions, signifying the coexistence of ZnO and rGO with carbon, oxygen, and zinc contents of 78.98%, 17.46%, and 3.56%, respectively. The investigations involved the photoelectrochemical profiles of methylene blue organic dyes at different concentrations, ranging from 0.5 ppm to 3.0 ppm. The acquired findings offer valuable understanding into the photoelectrocatalytic effectiveness of the composite electrodes containing rGO-ZnO, suggesting their potential use in potential scenarios involving the revitalization of the environment in industrial water systems.

Hierarchical Bimetallic AgPt Nanoferns as High-Performance Catalysts for Selective Acetone Hydrogenation to Isopropanol.

A combinative effect of two or more individual material properties, such as lattice parameters and chemical properties, has been well-known to generate novel nanomaterials with special crystal growth behavior and physico-chemical performance. This paper reports unusually high catalytic performance of AgPt nanoferns in the hydrogenation reaction of acetone conversion to isopropanol, which is several orders higher compared to the performance shown by pristine Pt nanocatalysts or other metals and metal-metal oxide hybrid catalyst systems. It has been demonstrated that the combinative effect during the bimetallisation of Ag and Pt produced nanostructures with a highly anisotropic morphology, i.e., hierarchical nanofern structures, which provide high-density active sites on the catalyst surface for an efficient catalytic reaction. The extent of the effect of structural growth on the catalytic performance of hierarchical AgPt nanoferns is discussed.