Photodetection Properties of CdS/Si Heterojunction Prepared by Pulsed Laser Ablation in DMSO Solution for Optoelectronic Application.

The high-quality n-type CdS on a p-type Si (111) photodetector device was prepared for the first time by a one-pot method based on an ns laser ablation method in a liquid medium. Cadmium target was ablated in DMSO solution, containing sulfur precursor, and stirred, assisting in 1D-growth, to create the sulfide structure as CdS nano-ropes form, followed by depositing on the Si-substrate by spin coating. The morphological, structural, and optical characteristics of the CdS structure were examined using X-ray diffraction, transmission, and scanning electron microscopy, photoluminescence, and UV-VIS spectroscopy. From X-ray diffraction analysis, the growing CdS spheres have a good crystal nature, with a high purity and desired c-axis orientation along the (002) plane, and the crystallinity was around 30 nm. According to optical characterization, high transparency was found in the visible-near-infrared areas of the electromagnetic spectrum, and the CdS spheres have a direct optical energy band gap of 3.2 eV. After that, the CdS/Si hetero-structured device was found to be improved remarkably after adding CdS. It showed that the forward current is constantly linear, while the dark current is around 4.5 µA. Up to a bias voltage of 4 V, there was no breakdown, and the reverse current of the heterojunctions somewhat increased with reverse bias voltage, while the photocurrent reached up to 580 and 690 µA for using 15 and 30 W/cm2 light power, respectively. Additionally, the ideal factors for CdS/Si heterojunction were 3.1 and 3.3 for 15 and 30 W/cm2 light power, respectively. These results exhibited high performance compared to the same heterojunction produced by other techniques. In addition, this opens the route for obtaining more enhancements of these values based on the changing use of sulfide structures in the heterojunction formation.

Effect of CuO Nanoparticles on the Optical, Structural, and Electrical Properties in the PMMA/PVDF Nanocomposite.

A polymeric nanocomposite film, composed of PMMA/PVDF and different amounts of CuO NPs, was successfully prepared using the casting method to enhance its electrical conductivity. Various techniques were employed to investigate their physicochemical properties. The addition of CuO NPs causes a noticeable difference in the intensities and locations of vibrational peaks in all bands, confirming the incorporation of CuO NPs inside the PVDF/PMMA. In addition, the broadening of the peak at 2θ = 20.6° becomes more intense with increasing amounts of CuO NPs, confirming the increase in the amorphous characteristic of PMMA/PVDF incorporated with CuO NPs in comparison with PMMA/PVDF. Furthermore, the image of the polymeric structure exhibits a smoother shape and interconnection of pore structure associated with spherical particles that agglomerate and give rise to a web-like organization that becomes a matrix. Increasing surface roughness is responsible for an increasing surface area. Moreover, the addition of CuO NPs in the PMMA/PVDF leads to a decrease in the energy band gap, and further increasing the additional amounts of CuO NPs causes the generation of localized states between the valence and conduction bands. Furthermore, the dielectric investigation shows an increase in the dielectric constant, dielectric loss, and electric conductivity, which may be an indication of an increase in the degree of disorder that confines the movement of charge carriers and demonstrates the creation of an interconnected percolating chain, enhancing its conductivity values compared with that without the incorporation of a matrix.

Photocatalytic Performance Improvement by Doping Ag on ZnO/MWCNTs Nanocomposite Prepared with Pulsed Laser Ablation Method Based Photocatalysts Degrading Rhodamine B Organic Pollutant Dye.

ZnO/MWCNTs nanocomposite has significant potential in photocatalytic and environmental treatment. Unfortunately, its photocatalytic efficacy is not high enough due to its poor light absorbance and quick recombination of photo-generated carriers, which might be improved by incorporation with noble metal nanoparticles. Herein, Ag-doped ZnO/MWCNTs nanocomposite was prepared using a pulsed laser ablation approach in the liquid media and examined as a degradable catalyst for Rhodamine B. (RhB). Different techniques were used to confirm the formation of the nanostructured materials (ZnO and Ag) and the complete interaction between them and MWCNTs. X-ray diffraction pattern revealed the hexagonal wurtzite crystal structure of ZnO and Ag. Additionally, UV-visible absorption spectrum was used to study the change throughout the shift in the transition energies, which affected the photocatalytic degradation. Furthermore, the morphological investigation by a scanning electron microscope showed the successful embedding and decoration of ZnO and Ag on the outer surface of CNTs. Moreover, the oxidation state of the formed final nanocomposite was investigated via an X-ray photoelectron spectrometer. After that, the photocatalytic degradations of RhB were tested using the prepared catalysts. The results showed that utilizing Ag significantly impacted the photo degradation of RhB by lowering the charge carrier recombination, leading to 95% photocatalytic degradation after 12 min. The enhanced photocatalytic performance of the produced nanocomposite was attributed to the role of the Ag dopant in generating more active oxygen species. Moreover, the impacts of the catalyst amount, pH level, and contact time were discussed.

Ag/ZnO Thin Film Nanocomposite Membrane Prepared by Laser-Assisted Method for Catalytic Degradation of 4-Nitrophenol.

Zinc oxide thin film (ZnO thin film) and a silver-doped zinc oxide nanocomposite thin film (Ag/ZnO thin film) were prepared by the technique of the pulsed laser deposition at 600 °C to be applicable as a portable catalytic material for the removal of 4-nitrophenol. The nanocomposite was prepared by making the deposition of the two targets (Zn and Ag), and it was analyzed by different techniques. According to the XRD pattern, the hexagonal wurtzite crystalline form of Ag-doped ZnO NPs suggested that the samples were polycrystalline. Additionally, the shifting of the diffraction peaks to the higher angles, which denotes that doping reduces the crystallite size, illustrated the typical effect of the dopant Ag nanostructure on the ZnO thin film, which has an ionic radius less than the host cation. From SEM images, Ag-doping drastically altered the morphological characteristics and reduced the aggregation. Additionally, its energy band gap decreased when Ag was incorporated. UV spectroscopy was then used to monitor the catalysis process, and Ag/ZnO thin films had a larger first-order rate constant of the catalytic reaction K than that of ZnO thin film. According to the catalytic experiment results, the Ag/ZnO thin film has remarkable potential for use in environmentally-favorable applications.

Removal of Ni(II) Ions by Poly(Vinyl Alcohol)/Al2O3 Nanocomposite Film via Laser Ablation in Liquid.

Al2O3-poly(vinyl alcohol) nanocomposite (Al2O3-PVA nanocomposite) was generated in a single step using an eco-friendly method based on the pulsed laser ablation approach immersed in PVA solution to be applicable for the removal of Ni(II) from aqueous solution, followed by making a physicochemical characterization by SEM, XRD, FT-IR, and EDX. After that, the effect of adsorption parameters, such as pH, contact time, initial concentration of Ni(II), and medium temperature, were investigated for removal Ni(II) ions. The results showed that the adsorption was increased when pH was 5.3, and the process was initially relatively quick, with maximum adsorption detected within 90 min of contact time with the endothermic sorption process. Moreover, the pseudo-second-order rate kinetics (k2 = 9.9 × 10-4 g mg-1 min-1) exhibited greater agreement than that of the pseudo-first-order. For that, the Ni(II) was effectively collected by Al2O3-PVA nanocomposite prepared by an eco-friendly and simple method for the production of clean water to protect public health.

Multifunctional leather surface embedded with zinc oxide nanoparticles by pulsed laser ablation method.

A simple procedure was used to generate and decorate leather structures with different amounts from zinc oxide (ZnO) nanoparticles to produce multifunctional leather structure by pulsed laser ablation method in liquid media based on changing the ablation time in just one-pot method. The impact of varying concentrations of ZnO nanoparticles embedded on the surface of leather on water resistance, water vapor permeability, mechanical characteristics, and UV-shielding efficiency was examined by different characterization techniques like X-ray diffraction, surface area, UV-visible spectroscopy, scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy, and thermogravimetric analysis. The results showed that the combination between the external functional groups of leather with ZnO nanoparticles was discovered. ZnO nanoparticles effectively coated the surface of leather tissue, as seen by SEM images, and their form a spherical morphology. Leather with ZnO nanoparticles added had the highest capacity to kill Escherichia coli bacteria, exceeding leather without modification and ZnO nanoparticles alone in 50-hr incubation. In addition, the incubation period had a substantial impact on the suppression of Staphylococcus aureus bacteria growth by leather samples.